Ballistic resistant panel for vehicle door

ABSTRACT

A ballistic resistant panel can be configured to be quickly and easily installed in a vehicle door. The ballistic resistant panel can include a plurality of ballistic sheets arranged in a stack. The stack can have an outer perimeter sized to fit within a cavity of the vehicle door. The panel can include a cover disposed over the stack, and the cover can be sealed around a perimeter of the stack to form a waterproof barrier that prevents moisture from reaching and altering the performance of the ballistic sheets. At least one anti-wear strip can be adhered to an outer surface of the cover. The anti-wear strip can provide a low friction surface that protects the panel from damage caused by moving internal door components, such as moving window components that repeatedly rub against the panel.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application No.62/006,255, filed Jun. 1, 2014 and is a continuation-in-part of U.S.patent application Ser. No. 14/322,931, filed Jul. 3, 2014, which claimsthe benefit of U.S. Provisional Application No. 61/842,937, filed Jul.3, 2013, and U.S. Provisional Application No. 61/903,337, filed Nov. 12,2013, all of which are hereby incorporated by reference as if fully setforth in this description.

BACKGROUND

Ballistic resistant panels can safeguard people and property fromballistic threats, such as projectiles. Ballistic resistant panels canbe incorporated into vests to protect people from projectiles, such asbullets or shrapnel, and can be incorporated into vehicle doors andfloors to prevent occupants and equipment from projectiles and blasts.Ballistic resistant panels are commonly made of woven fabrics consistingof high performance fibers, such as aramid fibers. When struck by aprojectile, fibers in the woven fabric dissipate impact energytransferred from the projectile by stretching and breaking, therebyproviding a certain level of ballistic protection.

Existing ballistic resistant panels are often made of a stack of wovenballistic sheets stitched together by a sewing process that requires anindustrial sewing machine. The level of ballistic protection provided bythe panel is largely dictated by the type of fibers in the wovenballistic sheets, the number of woven ballistic sheets in the stack, andthe stitching pattern used to bind the woven ballistic sheets togetherinto a panel. A wide variety of stitching patterns are used in existingpanels, including quilt stitches, radial stitches, row stitches, and boxstitches.

When a projectile strikes a panel made of a stack of woven ballisticsheets bound by stitching, each woven ballistic sheet dissipates acertain portion of the energy of the projectile as the projectile passesthrough each sheet. Within each woven ballistic sheet, individual fibersstretch and break apart as the projectile penetrates the sheet. Theimpact energy absorbed by a struck fiber will be transferred anddissipated to nearby fibers at crossover points where the fibers areinterwoven. Also, individual stitches will stretch and break apart asthe projectile enters the panel, thereby dissipating impact energy fromthe projectile and acting as a sacrificial element of the panel.

Due to the sacrificial nature of the fibers and stitches, the panel willbe severely damaged when struck by a projectile. Visual inspection ofthe panel will typically reveal significant damage to the wovenballistic sheets and to stitches both at the impact location and thesurrounding area. If a second projectile strikes the panel at or nearthe first impact location, the panel will not effectively stop thesecond projectile, and the second projectile will pass through the paneland into a person or property behind the panel. Therefore, existingpanels do not provide reliable protection against multiple projectilesstriking the panel in close proximity, which is a common threat posed bymany automatic and semi-automatic weapons. For at least this reason,existing ballistic resistant panels are not well-suited for applicationswhere multi-round capability is required.

SUMMARY

This disclosure relates to ballistic resistant panels for vehicle doorsand methods of rapidly installing ballistic resistant panels in vehicledoors.

In some examples, a ballistic resistant panel can be installed within avehicle door between an outer door structure and a side window of thevehicle door. The panel can include a plurality of ballistic sheetsarranged in a stack. The stack can have an outer perimeter sized to fitwithin a cavity of the vehicle door. The panel can include a coverdisposed over the stack. The cover can be sealed around the perimeter ofthe stack to form a waterproof barrier that prevents moisture on anouter surface of the cover from reaching the plurality of ballisticsheets. The panel can include an excess cover portion extending from atop edge of the ballistic resistant panel. The excess cover portion canbe securable against a lip of an outer door structure by a weatherstrip.The panel can include at least one anti-wear strip adhered to the outersurface of the cover. The anti-wear strip can be configured to provide alow friction surface against which a moving part within the vehicle doormay repeatedly contact without breaching the cover.

The anti-wear strip can include high-density polyethylene orpolycarbonate. The panel can include an adhesive layer positionedbetween the outer surface of the cover and an inner surface of theanti-wear strip. The adhesive layer can serve to adhere the anti-wearstrip to the outer surface to the cover. The cover can include nylonfabric coated with polyurethane, silicone, polypropylene, polyethylene,or polyvinylchloride. The cover can include rubber, nylon fabric, rayonfabric, ripstop nylon fabric, polyvinyl chloride (PVC), polyurethane, orsilicone elastomer.

The ballistic resistant panel can undergo a heated vacuum baggingprocess to decrease its thickness and to promote at least partialbonding between adjacent ballistic sheets in the plurality of ballisticsheets to improve ballistic performance. The stack of ballistic sheetscan include aramid, para-aramid, meta-aramid, polyolefin, orthermoplastic polyethylene fibers. The ballistic sheets can haveuni-ply, 0/90 x-ply, or 0/90/0/90 double x-ply configurations.

The plurality of ballistic sheets can include a first, second, and thirdplurality of ballistic sheets. The first plurality of ballistic sheetscan include aramid fibers and a first resin with a first meltingtemperature. The first melting temperature can be about 215-240 degreesF. The first resin can be polyethylene. The second plurality ofballistic sheets can be adjacent to the first plurality of ballisticsheets. The second plurality of ballistic sheets can include aramidfibers and a second resin with a second melting temperature. The secondmelting temperature can be about 255-295, 275-310, or 295-330 degrees F.The second resin can be polypropylene. The first plurality of ballisticsheets can include 1-10, 10-20, or 20-30 ballistic sheets. The secondplurality of ballistic sheets can include 1-10, 10-20, or 20-30ballistic sheets.

The ballistic resistant panel can have a thickness less than or equal to0.24 inches and an areal density less than or equal to 1.38 lb/ft². Theballistic resistant panel can have V₅₀ ratings of 1600 ft/sec or greaterfor .44 Magnum lead bullet having a nominal mass of 15.55 grams and 1720ft/sec or greater for a 9 mm full metal jacketed bullet having a nominalmass of 8.0 grams. The ballistic resistant panel can have a ballisticperformance that meets or exceeds level III-A requirements set forth inNIJ Standard-0101.06.

In some examples, a method of rapidly installing a ballistic resistantpanel within a vehicle door can be accomplished without removing a sidewindow or trim panel from the vehicle door. The method can includeremoving a side window weatherstrip from the vehicle door. The methodcan include inserting a ballistic resistant panel through a gap in thevehicle door. The gap can be located between an outer door structure anda side window of the vehicle door. The ballistic resistant panel caninclude a fabric cover. The fabric cover can include an excess coverportion along a top edge of the ballistic resistant panel. The methodcan include pressing a bottom edge of the ballistic resistant paneldownward into a V-shaped channel formed along a bottom edge of thevehicle door where the outer door structure is joined to an inner doorstructure. The method can include folding the excess cover portion overa lip of the outer door structure. The method can include reinstallingthe side window weatherstrip onto the lip of the outer door structureand capturing the excess cover portion between the lip and theweatherstrip. The method can include lowering the side window of avehicle door prior to inserting the ballistic resistant panel throughthe gap in the vehicle door.

In yet another example, a method of manufacturing a ballistic resistantpanel for insertion in a vehicle door can include providing a pluralityof ballistic sheets arranged to form a stack of ballistic sheets,covering the stack of ballistic sheets with a cover, inserting the stackof ballistic sheets and cover into a vacuum bag, evacuating air from thevacuum bag, heating the stack of ballistic sheets and cover in thevacuum bag to a predetermined temperature for a predetermined duration,and adhering an anti-wear strip to an outer surface of the fabric cover.The anti-wear strip can be configured to provide a low friction surfaceagainst which a moving part within the vehicle door may repeatedlycontact without breaching the fabric cover of the ballistic resistantpanel.

The predetermined temperature can be about 250-550, 225-550, 225-350,250-300, 250-275, 265-275, 225-250, or 200-240 degrees F. Thepredetermined duration can be about 1, 5, 15-30, 30-60, 45-60, 60-120,120-240, or 240-480 minutes. The method can include applying apredetermined pressure to the stack of ballistic sheets in the vacuumbag for a second predetermined duration. The predetermined pressure canabout 10-100, 50-75, 75-100, 100-500, 500-1,000, 1,000-2,500,2,500-15,000, or 15,000-30,000 psi, and the second predeterminedduration can be about 1, 5, 15-30, 30-60, 45-60, 60-120, 120-240, or240-480 minutes. The heat and pressure can be applied concurrently insome examples.

Providing the plurality of ballistic sheets arranged to form a stack ofballistic sheets can include providing a first plurality of ballisticsheets, a second plurality of ballistic sheets, and a third plurality ofballistic sheets. The first plurality of ballistic sheets can have afirst resin with a melting temperature of about 215-240, 240-265,265-295, or 295-340 degrees F. The second plurality of ballistic sheetscan be adjacent to the first plurality of ballistic sheets. The secondplurality of ballistic sheets can include a second resin with a meltingtemperature of about 255-295, 295-330, 330-355, or 355-375 degrees F.The third plurality of ballistic sheets can be adjacent to the secondplurality of ballistic sheets. The third plurality of ballistic sheetscan include a third resin with a melting temperature of about 215-240,240-265, 265-295, or 295-340 degrees F.

The first plurality of ballistic sheets can include 1-10, 10-20, or20-30 x-ply ballistic sheets. The first plurality of ballistic sheetscan include aramid fibers, and the first resin can be polyethylene. Thesecond plurality of ballistic sheets can include 1-10, 10-20, or 20-30x-ply ballistic sheets. The second plurality of ballistic sheets caninclude aramid fibers, and the second resin can include polypropylene.The third plurality of ballistic sheets can include 1-10, 10-20, or20-30 x-ply ballistic sheets. The third plurality of ballistic sheetscan include aramid fibers, and the third resin can include polyethylene.

Additional objects and features of the invention are introduced below inthe Detailed Description and shown in the drawings. While multipleembodiments are disclosed, still other embodiments will become apparentto those skilled in the art from the following Detailed Description,which shows and describes illustrative embodiments. As will be realized,the disclosed embodiments are susceptible to modifications in variousaspects, all without departing from the scope of the present disclosure.Accordingly, the drawings and detailed description are to be regarded asillustrative in nature and not restrictive.

This Summary is provided to introduce a selection of concepts in asimplified form that are further described in the Detailed Descriptionbelow. This Summary is not intended to identify key features oressential features of the claimed subject matter, nor is it intendedthat this Summary be used to limit the scope of the claimed subjectmatter. Furthermore, the claimed subject matter is not limited toimplementations that solve any or all disadvantages noted in any part ofthis disclosure.

BRIEF DESCRIPTIONS OF DRAWINGS

FIG. 1 shows a process of fabricating a roll of ballistic sheet materialusing a plurality of fibers drawn from creels.

FIG. 2 shows a process of forming a 0/90 x-ply ballistic sheet from tworolls of unidirectional ballistic sheet material.

FIG. 3 shows a process of forming a 0/90 x-ply ballistic sheet from twounidirectional ballistic sheets.

FIG. 4 shows an enlarged view of a portion of a 0/90 x-ply ballisticsheet containing two unidirectional ballistic sheets bonded by twolayers of resin film.

FIG. 5 shows a carrier vest with a pouch containing a flexibleballistic-resistant panel (e.g. soft armor) positioned behind a rigid orsemi-rigid ballistic resistant member (e.g. hard armor).

FIG. 6 shows a prior art bullet-proof vest with an edge seam undone toexpose a stack of ballistic sheets fanned out with no partial or fullbonding between adjacent sheets.

FIG. 7 shows a process of arranging a stack of ballistic sheetsaccording to a two-dimensional pattern inside a waterproof cover priorto a vacuum bagging process.

FIG. 8 shows two stacks of ballistic resistant sheets, each wrapped in awaterproof cover and ready for insertion into a vacuum bag sized toaccommodate several flexible ballistic resistant panels during a vacuumbagging process.

FIG. 9 shows a vacuum bagging process employing a vacuum bag sized toaccommodate one flexible ballistic resistant panel.

FIG. 10 is a cross-sectional side view of a flexible ballistic resistantvehicle door panel containing a plurality of ballistic sheets, each ofthe plurality of ballistic sheets being formed of an arrangement offibers that defines a two-dimensional pattern, the first plurality ofballistic sheets being stacked according to the two-dimensional pattern.

FIG. 11 is a cross-sectional side view of a flexible ballistic resistantvehicle door panel containing a stack of ballistic sheets and awaterproof cover where the stack of ballistic sheets includes a firstplurality of ballistic sheets, a second plurality of ballistic sheetsadjacent to the first plurality of ballistic sheets, and a thirdplurality of ballistic sheets adjacent to the second plurality ofballistic sheets.

FIG. 12 is a cross-sectional side view of a flexible ballistic resistantvehicle door panel including a stack of ballistic sheets and awaterproof cover where the stack of ballistic sheets includes a firstplurality of ballistic sheets, a second plurality of ballistic sheetsadjacent to the first plurality of ballistic sheets, and a thirdplurality of ballistic sheets adjacent to the second plurality ofballistic sheets.

FIG. 13 is a cross-sectional side view of a flexible ballistic resistantvehicle door panel including a stack of ballistic sheets and awaterproof cover where the stack of ballistic sheets includes a firstplurality of ballistic sheets, a second plurality of ballistic sheetsadjacent to the first plurality of ballistic sheets, and a thirdplurality of ballistic sheets adjacent to the second plurality ofballistic sheets.

FIG. 14 is a cross-sectional side view of a ballistic resistant vehicledoor panel having two flexible ballistic resistant panels encased by acover.

FIG. 15 shows a cross-section side view of a ballistic resistant vehicledoor panel having two stacks of ballistic sheets combined within asingle waterproof cover to form a combined stack of ballistic sheetsincluding a first plurality of ballistic sheets, a second plurality ofballistic sheets, a third plurality of ballistic sheets, a fourthplurality of ballistic sheets, and a fifth plurality of ballisticsheets.

FIG. 16 is a side cross-sectional view of a ballistic resistant vehicledoor panel having a stack of three flexible ballistic resistant panelswithin a waterproof cover, where each panel is also encased in its owncover.

FIG. 17 shows a vehicle door including an interior trim panel and a sidewindow.

FIG. 18 shows an exterior surface of the vehicle door of FIG. 17.

FIG. 19 shows the vehicle door of FIG. 17 with a side window partiallylowered.

FIG. 20 shows a front view of a ballistic resistant vehicle door panelconfigured for installation within a vehicle door of FIG. 17 between anouter door structure and a side glass window of the vehicle door.

FIG. 21 shows a top perspective view of the ballistic resistant vehicledoor panel of FIG. 20.

FIG. 22 shows a front view of a ballistic resistant vehicle door panelconfigured for installation within a vehicle door between an outer doorstructure and a side glass window of the vehicle door.

FIG. 23 shows a perspective view of the ballistic resistant vehicle doorpanel of FIG. 20 partially installed through a gap in the vehicle doorof FIG. 17, the gap located between the outer door structure and theside glass window of the vehicle door.

FIG. 24 shows a perspective view of the ballistic resistant vehicle doorpanel of FIG. 20 nearly fully installed through a gap in the vehicledoor of FIG. 17, the gap located between the outer door structure andthe side glass window of the vehicle door

FIG. 25 shows a perspective view of the ballistic resistant vehicle doorpanel of FIG. 20 fully installed through a gap in the vehicle door ofFIG. 17, the gap located between the outer door structure and the sideglass window of the vehicle door

FIG. 26 shows an enlarged view of FIG. 25 where the ballistic resistantvehicle door panel is fully installed through the gap in the vehicledoor but prior to a weatherstrip being reinstalled proximate the gap tosecure an excess cover portion of the ballistic resistant panel againsta lip of the outer door structure.

FIG. 27 shows an enlarged perspective view of the vehicle door where theballistic resistant panel is fully installed in the vehicle door and theweatherstrip is reinstalled proximate the gap to secure the excess coverportion of the ballistic resistant panel against the lip of the outerdoor structure.

DETAILED DESCRIPTION

There is a strong demand among law enforcement and military departmentsfor affordable ballistic resistant panels that can be inserted quicklyand easily into vehicle doors to protect vehicle occupants (e.g. policeofficers) from ballistic threats. But despite this strong demand,manufacturers of ballistic resistant panels have thus far been unable todevelop an affordable panel that can be quickly and easily installed ina vehicle door. Existing products require complete disassembly of thevehicle door, including removal of the side window, speaker, windowtrack, and door trim. Some products also require a skilled installer todrill mounting holes in the door to accommodate fasteners. It can oftentake a skilled installer several hours to install a single panel, whichresults in significant installation costs to the vehicle owner,especially when panels must be installed in two or more doors. Inaddition to these drawbacks, existing panels also have relatively poorballistic performance, since they are nothing more than a stack ofballistic sheets stitched together to form a panel. Moreover, existingpanels lack a protective cover, which leaves the ballistic sheetsexposed to dust, dirt (which is common in dessert regions where duststorms are prevalent), and moisture that can enter the door cavity andwork its way between adjacent sheets, and potentially degrade theballistic performance of the panel. The lack of a protective cover alsoleaves the ballistic sheets exposed to damage resulting from rubbingagainst certain door components, such as window bolts, which mayrepeatedly go up and down relative to the panel as a user actuates apower window control.

In view of the forgoing discussion, it is desirable to develop aballistic resistant panel that can be inserted quickly and easily into avehicle door without requiring any special skills or power tools. Theballistic resistant panel 100 described herein can be installed in avehicle door in about 5-15 minutes by an individual with no priortraining who is following a simple set of instructions. Duringproduction, the ballistic resistant panel 100 is subjected to anadvanced manufacturing process, detailed herein, which results insignificantly improved ballistic performance when compared to existingstitched panels having an identical number of ballistic sheets. Theballistic resistant panel 100 can include a covering 1105 that protectsthe ballistic sheets from moisture and wear. The ballistic resistantpanel 100 can also include an anti-wear strip 105 affixed to an outersurface of the panel. The anti-wear strip 105 can provide a low frictionsurface against which certain moving door components, such as windowbolts, are designed to rub without causing any damage to the panel'scover 1105.

The ballistic resistant panel 100 can be installed quickly and easily ina vehicle door 1700 with relatively little disassembly of the door. FIG.17 shows a stock vehicle door 1700 prior to installation of theballistic resistant vehicle panel 100. A weatherstrip 1760 affixed to alip 1730 on the outer door structure 1715 can also be removed to exposea gap 1720 located between an outer door structure 1715 and the sidewindow 1705. In some cases the weatherstrip 1760 may be affixed to theouter door structure 1715 with one or more fasteners, and in othercases, the weatherstrip may not be affixed to the outer door structure1715 with any fasteners, as shown in FIG. 18. Where no fasteners areused, the weatherstrip 1760 may simply employ an interference fit toremain engaged with the lip 1730 of the outer door structure 1715. Inthese instances, an installer can simply pry the weather strip free fromthe lip 1730 by starting at one end of the weatherstrip 1760 and thenworking along the length of the weatherstrip until it is completely freeof the lip.

Once the weatherstrip 1760 has been removed, a gap 1720 will be visiblebetween the lip 1730 of the outer door structure 1715 and the sidewindow 1705. The gap 1720 will be large enough to receive the ballisticresistant panel 100. As shown in FIGS. 20-22, the ballistic resistantpanel 100 can include one or more anti-wear strips 105 adhered by anadhesive, or attached by any suitable method, to a front surface of acover 1105 of the panel. The anti-wear strips 105 can prevent movingcomponents within the vehicle door 1700 from damaging the panel 100 overtime due to repeated contact or rubbing. The anti-wear strips 105 canprovide a low friction surface, which certain components, such as windowcomponents, can slide against as the window 1705 moves up and down. Theanti-wear strips 105 can have high wear-resistance and can prevent, forexample, window bolts from gouging, tearing, or puncturing the cover1105 of the panel over time with repeated actuation of the window. Theanti-wear strips 105 can have any suitable shape and thickness. Theshape, thickness, and location of the anti-wear strips 105 may bedictated by vehicle make and model and by the type and location of innerdoor components within a specific vehicle's door. Consequently, theshape, thickness, or location of anti-wear strips on a panel 100designed for a DODGE CHARGER can differ from the shape, thickness, orlocation of anti-wear strips on a panel designed for a FORD EXPLORER.The anti-wear strips 105 can be made of any suitable polymer materialthat can be reliably adhered to the outer surface of the cover 1105. Insome examples, the anti-wear strips can be made of high-densitypolyethylene (HDPE), perfluoroalkoxy (PFA), fluorinated ethylenepropylene (FEP), or polytetrafluoroethylene (PTFE). In other examples,the anti-wear strips can be made of polycarbonate or any other suitablelow friction thermoplastic. In still other examples, the anti-wearstrips 105 can be made of a non-polymer material, such as a metal,having a low friction surface with high wear resistance.

In some examples, the anti-wear strips 105 can be adhered to the backsurface 115 of the cover 1105 by a lamination process. An adhesive layer(e.g. liquid or film adhesive) can be applied between the back surface115 of the cover 1105 and the mating surface of the anti-wear strip 105.A heated roller of a laminator can then apply heat and pressure toactivate the adhesive and bond the anti-wear strip 105 to the panel 100.In some examples, the ballistic resistant panel can include anti-wearstrips on a front surface 120 of the cover 1105. In addition toprotecting the panel from wear against inner door components, theanti-wear strips can also ease installation of the panel into a cavitywithin the vehicle door 1700.

FIGS. 23-26 show a progression of figures chronicling an installationprocess. In FIG. 23, the ballistic resistant panel 100 is being fed intothe gap 1720 located between the outer door structure 1715 and the sidewindow 1705. As the panel 100 is fed into a gap, the panel will slideagainst the side window as it is pushed downward into the cavity of thevehicle door. The smooth surface of the side window 1705 easesinstallation and guides the panel 100 down into the door cavity. In somevehicles, it may be helpful to have the window completely down to easeinstallation of the panel 100. In other vehicles, as shown in FIG. 19,it may be desirable to keep the window up a certain distance 1725, suchas 2-4, 4-6, 6-8, or 8-10 inches up to ease installation of the panel100. In this example, an outer surface of the window glass 1705 canprovide a low friction surface that aids in guiding the ballisticresistant panel 100 into place within the vehicle door 1700.

In FIG. 24, the ballistic resistant panel 100 is more than half wayinstalled in the door. In FIGS. 25 and 26, the ballistic resistant panelis fully installed in the door, but the final step of reinstalling theweatherstrip 1760 has not yet been completed. On most vehicle doors1700, where the outer door structure 1715 joins (e.g. is welded to) theinner door structure 1770 along the bottom edge 1785 of the door, aV-shaped channel 1785 is typically formed along the bottom edge of thedoor, with the opening of the V facing upward. As the ballisticresistant panel 100 is pressed downward into the cavity of the vehicledoor 1700, the bottom edge 140 of the panel 100 will seat in theV-shaped channel located along the bottom edge 1785 of the door 1700,thereby immobilizing the bottom edge of the panel 100 and eliminatingthe need for any fasteners to secure the panel to the lower portion ofthe door. The bottom edge 140 of the panel 100 is effectively pinch onan inner surface and outer surface by opposing surfaces of the V-shapedchannel located along the bottom edge 1785 of the door 1700.

As shown in FIGS. 25 and 26, the cover 1105 can include an excess coverportion 110 extending from a top edge of the panel 100. Once the panel100 has been installed in the vehicle door 1700, and the bottom edge 140of the panel has been seated in the V-shaped channel located at thebottom edge 1785 of the door 1700, the excess cover portion 110 can befolded over the lip 1730 of the outer door structure 1715, and theweatherstrip 1760 can be reinstalled over the lip, effectively capturingthe excess cover portion between the lip of the outer door structure andthe weatherstrip. This method of attaching the panel 100 to the door1700 results in significant time savings compared to existingapproaches. In addition, because no fasteners or drills are required,this method dramatically reduces the likelihood of installation errorsand product returns. Moreover, when the time comes to uninstall thepanel 100 from the vehicle door 1700, the uninstallation process is asquick and easy as the installation process and results in no damage tothe panel or the vehicle door 1700. Consequently, after an inspectionconfirming that the panel 100 has not sustained any damage ordegradation during its first deployment, the panel can be transferred toa second vehicle that is the same make and model as the first vehicle inwhich the panel was installed. This capability is of particular interestto law enforcement departments who regularly decommission policecruisers and attempt to salvage and reuse as many aftermarket componentsas possible on new police cruisers.

A method of rapidly installing a ballistic resistant panel 100 within avehicle door 1700 can be accomplished without removing a side window1705 or trim panel 1710 from the vehicle door. The method can includeremoving a side window weatherstrip 1760 from the vehicle door 1700. Themethod can include inserting a ballistic resistant panel 100 through agap 1720 in the vehicle door 1700, as shown in FIGS. 23 and 24. The gap1720 can be located between an outer door structure 1715 and a sidewindow 1705 of the vehicle door, as shown in FIG. 26. The ballisticresistant panel 100 can include a fabric cover 1105, as shown in FIGS.20-22. The fabric cover 1105 can include an excess cover portion 110along a top edge of the ballistic resistant panel. The method caninclude pressing a bottom edge 140 of the ballistic resistant panel 100downward into a V-shaped channel formed along a bottom edge 1785 of thevehicle door 1700 where the outer door structure 1715 is joined to aninner door structure 1710. The method can include folding the excesscover portion 110 over a lip 1730 of the outer door structure 1715. Theexcess cover portion 110 can be made of flexible fabric and can extendabout 0.5-1, 0.75-2, or 1.5-3 inches above the ballistic resistantportion of the panel 100 to provide sufficient fabric to extend up andover the the lip 1730 of the door and rest against an exterior surfaceof the outer door structure 1715. The method can include reinstallingthe side window weatherstrip 1760 onto the lip 1730 of the outer doorstructure 1715 and capturing the excess cover portion 110 between thelip 1730 and the weatherstrip 1760, as shown in FIG. 27. Once theweatherstrip 1760 has been installed, the panel 100 is effectivelycaptured along a top edge and a bottom edge, thereby completinginstallation and securing of the panel within the vehicle door.

For some vehicle makes and models, the method can include lowering theside window 1705 of a vehicle door 1700 prior to inserting the ballisticresistant panel 100 through the gap 1720 in the vehicle door, as shownin FIGS. 23-27. In these instances, lowering the window 1705 prior toinserting the panel 100 can ease installation, since the panel can beinserted downward through the gap 1720 as it glides against an outersurface of the side window 1705. This approach can reduce the risk ofthe panel 100 catching on a mechanism inside the door and frustratinginstallation. The side window 1705 can also help to guide the panel 100into place within the vehicle door 1700 as the panel is pressed downwarduntil the bottom edge seats in the V-shaped channel formed along thebottom edge 1785 of the door.

In some instances, the panel 100 may need to be first inserted downwardthrough the gap 1720, and once seated in the V-shaped channel, theentire panel may need to be shifted forward toward a front end of thevehicle to improve ballistic protection near a front edge of the vehicledoor. This approach may be needed where, due to a vehicle door'sirregular shape, a rectangular panel 100 is not suitable and a moresophisticated shape is needed. In examples, where repositioning of thepanel is required once the bottom edge 140 of the panel is seated in theV-shaped channel along the bottom edge of the door, the excess coverportion 110 can provide a suitable place to grab the panel to facilitaterepositioning.

In some instances, the panel 100 can contour to an inner surface of theouter door structure 1715. This can be accomplished by pre-forming thepanel 100 to have a curvature matching a curvature of the outer doorstructure 1715. In another example, once the bottom edge 140 of thepanel 100 is seated against in the V-shaped channel of the door,additional downward pressure can be applied along a top edge of thepanel 100, resulting in outward flexing of the panel in response to thevertical load. The panel 100 can flex outwardly and contour to the innersurface of the outer door structure 1715. Contouring the panel 100 tothe inner surface of the outer door structure 1715 can be desirable toprovide additional clearance between internal door mechanisms and thepanel 100, thereby reducing the likelihood of panel wear or othercomplications.

Ballistic Resistant Door Panel

Ballistic resistant panels 100 are described herein that havesignificantly better multi-shot capability than existing panels. Inaddition, the ballistic resistant panels described herein can belighter, thinner, more flexible, easier to conceal, and less expensiveto manufacture than existing panels. The panels described herein can bemade in a reversible configuration where either side of the panel canserve as a strike face, thereby avoiding risks associated with usererror. The panels described herein can prevent ricochet of projectiles(which is an inherent drawback of metal armor) by, for example,encapsulating the projective through controlled delamination and energyabsorption. The panels described herein can experience significantlyless back face deformation than existing panels when exposed to anidentical ballistic threat. Methods of manufacturing the ballisticresistant panels, as described herein, can involve one or more steps,including cutting ballistic sheets, stacking ballistic sheets, sealingballistic sheets within a waterproof cover, vacuum bagging a stack ofballistic sheets, heating a stack of ballistic sheets, applying pressureto a stack of ballistic sheets, cooling a stack of ballistic sheets,trimming a waterproof cover, and breaking-in the ballistic panel.

The ballistic resistant panels 100 described herein are capable ofabsorbing and dissipating energy from high-velocity impacts through oneor more of the following energy-absorbing mechanisms: spall formation,tensile fiber failure, fiber de-bonding, fiber pullout, and interlayerdelamination. The term “panel,” as used herein, can describe any3-dimensionally shaped ballistic resistant apparatus, including a flator contoured shape having any suitable perimeter shape, includingregular or irregular perimeter shapes. In some applications, the panel100 may include one or more openings. For example, if the panel is usedwithin a vehicle door 1700, the panel may include an opening toaccommodate a component located within the door, such as a wiringharness.

Wide Ranging Applications

The flexible ballistic resistant panels 100 described herein arelightweight and flexible and can be used in a wide range ofvehicle-related applications that require dissipation of impact energy.For instance, the flexible ballistic resistant panels 100 describedherein can serve as spall liners in tanks and other armored vehicles toprotect against, for example, the effects of high explosive squash head(HESH) anti-tank shells. Spall liners can serve as a secondary armor foroccupants and equipment within an armored vehicle having a primary armormade of steel, ceramic, aluminum, or titanium. In the event of an impactor explosion proximate an outer surface of the armored vehicle, thespall liner can prevent or reduce fragmentation into the vehicle cabin,which is desirable, since fragmentation can result in fragments flyinginto the vehicle cabin, which may cause more injury to vehicle occupantsthan the original explosion. When used as a spall liner, the ballisticresistant panels 100 can be positioned between exterior steel armorplating of the military vehicle and the cabin of the vehicle. To provideadequate protection against spall, it may be necessary to provide astack of ballistic resistant panels, where the stack includes one ormore ballistic panels 100 in combination.

The flexible ballistic resistant panels 100 described herein can beincorporated into vehicle doors, floors, firewalls, roofs, and seats toprotect the vehicle, occupants, equipment, and ammunitions in thevehicle from projectiles. Due to their light weight and low cost, thepanels 100 described herein can be incorporated into consumer vehicleswithout significantly reducing fuel economy or increasing vehicle cost.In addition to protecting against ballistic threats, the panels 100 mayimprove certain aspects of crash performance of vehicles. Due to theflexibility and thinness of the panels 100, a panel can be installedinto a vehicle door between a door window and window seal. This allowsexisting vehicles to be easily armored without needing to fullydisassemble the door panels. The flexible panel can be easily insertedinto a door cavity and can be contorted around door components. Due tothe relatively soft nature of the panels described herein, the panels donot cause unwanted noise or vibration.

No Stitching Required

An advantage of the flexible ballistic resistant panels 100 describedherein over existing panels is that no stitching is required tomanufacture the panels. Instead of stitching, combinations of processesdescribed herein (e.g. vacuum-bagging, applying heat, applying pressure)result in full or partial bonding between adjacent layers of ballisticsheets in the stack 1005. This full or partial bonding resists movementof the ballistic sheets relative to each other (similar to how a stitchwould) and improves performance of the panel when struck by aprojectile. Panels without stitching are far less labor intensive thanpanels with stitching and don't require access to industrial sewingmachines. Consequently, panels without stitching can be manufactured ata lower cost.

Ballistic Sheet Construction

A ballistic resistant panel can be made of one or more ballistic sheets.The term “sheet,” as used herein, can describe one or more layers of anysuitable material, such as a polymer, metal, fiberglass, or compositematerial, or combination thereof. Examples of polymers include aramids,para-aramids, meta-aramids, polyolefins, and thermoplasticpolyethylenes. Examples of aramids, para-aramids, meta-aramids includeNOMEX, KERMEL, KEVLAR, TWARON, NEW STAR, TECHNORA, HERACRON, andTEIJINCONEX. An example of a polyolefin is INNEGRA. Examples ofthermoplastic polyethylenes include TENSYLON from E. I. du Pont deNemours and Company, DYNEEMA from Dutch-based DSM, and SPECTRA fromHoneywell International, Inc., which are all examples ofultra-high-molecular-weight polyethylenes (UHMWPE). Examples of types ofglass fibers include A-glass, C-glass, D-glass, E-glass, E-CR-glass,R-glass, S-glass, and T-glass. Other suitable fibers include M5(polyhydroquinone-diimidazopyridine), which is both high-strength andfire-resistant.

A ballistic sheet 10 can be constructed using any suitable manufacturingprocess, such as extruding, die cutting, forming, pressing, weaving,rolling, etc. The sheet can include a woven or non-woven construction ofa plurality of fibers bonded by a resin, such as a thermoplasticpolymer, thermoset polymer, elastic resin, or other suitable resin. Inone example, the ballistic sheet 10 can include a plurality of aramidbundles of fibers 11 bonded by a resin containing 16, for example,polypropylene, polyethylene, polyester, or phenol formaldehyde. Theplurality of bundles of fibers 11 in the sheet 10 can be oriented in thesame direction, thereby creating a unidirectional fiber arrangement,known as a uni-ply ballistic sheet 10.

In some examples, the ballistic sheet 10 can include fibers 11 that arepre-impregnated with a resin, such as thermoplastic polymer, thermosetpolymer, epoxy, or other suitable resin. The fibers 11 can be arrangedin a woven pattern or arranged unidirectionally, as shown in FIG. 3. Theresin can be partially cured to allow for easy handling and storage ofthe ballistic sheet prior to formation of the panel. To prevent completecuring (e.g. polymerization) of the resin before the sheet 10 isincorporated into a panel, the ballistic sheet may require cold storage.

Certain ballistic sheets are described in U.S. Pat. No. 5,437,905, whichis hereby incorporated by reference in its entirety. FIG. 1 shows anexample method for forming an array from a plurality of bundles offibers 11. The bundles of fibers 11 can be supplied from a plurality ofyarn creels 12. The bundles of fibers 11 can pass through a comb guide13 where the bundles of fibers are arranged in a parallel orientationand formed into an array and passed over a resin application roller 15where a resin film 16, such as a thin polyethylene or polypropylene filmor other suitable film, is applied to one side of the array. The bundlesof fibers 11 may be twisted or stretched prior to passing over the resinapplication roller 15 to increase their tenacity. A pre-laminationroller 18 can then press the array of bundles of fibers 11 against theresin film 16, which is then pressed against a heated plate 19, whichcauses the resin film to adhere to the array. After heating, the bundlesof fibers 11 and the resin film 16 can be passed through a pair ofheated pinch rolls 20, 21 to form a ballistic sheet. The ballistic sheet10 can then be wound onto a roll 22.

As shown in FIGS. 2-4, two ballistic sheets, known as uni-ply, havingunidirectional arrangements of fibers 10 can be bonded together toproduce a configuration known as x-ply 25. X-ply 25 can include a firstballistic sheet 10 and a second ballistic sheet 30, each having atwo-dimensional arrangement of unidirectionally-oriented fibers 11. Thesecond ballistic sheet 30 can be arranged at a 90-degree angle withrespect to the first ballistic sheet 10, which is set to a referenceangle of 0-degrees, as shown in FIG. 3. This configuration is known as0/90 x-ply, where “0” and “90” denote the relative orientations (indegrees) of the bundles of fibers 11 within the first and secondballistic sheets (10, 30), respectively. The first ballistic sheet 10can be laminated to the second ballistic sheet 30 in the absence ofadhesives or bonding agents. Instead, a first thermoplastic film 16 andsecond thermoplastic resin film 17 can be bonded to the outer surfacesof the first and second ballistic sheets (10, 30) without penetration ofthe resin films into the bundles of fibers 11 or through the laminatedsheets from one side to the other. Through a process involving heat andpressure, as shown in FIG. 3, the resin films (16, 17) melt andsubsequently solidify to effectively laminate the uni-ply ballisticsheets (10, 30) to each other, as shown in FIG. 4, thereby producing a0/90 x-ply configuration.

Ballistic Sheet Resin

Ballistic sheets (e.g. 25) can be coated or impregnated with one or moreresins (e.g. 16). Certain resins, such as resins made of thermoplasticpolymers, may include long chain molecules. The chains of molecules maybe held close to each other by weaker secondary forces. Upon heating,the secondary forces may be reduced, thereby permitting sliding of thechains of molecules and resulting in visco-plastic flow and ease inmolding. Heating of the ballistic sheets (e.g. 25) may cause softeningof the resin, and the resin may become tacky as it softens. Softeningmay occur at the softening point, which is the temperature at which theresin softens beyond some arbitrary softness and can be determined, forexample, by the Vicat method (ASTM-D1525). Applying pressure to thestack of ballistic sheets 1005 when the resin is softened and tacky mayresult in a softened resin layer on a first ballistic sheet contactingand adhering to a second ballistic sheet that is adjacent to the firstballistic sheet, and when the panel 100 is subsequently cooled and thetemperature of the resin is reduced, the first and second ballisticsheets may be partially or fully bonded to each other. In one example,ballistic sheets in a panel may be coated or impregnated with apolypropylene resin, and the polypropylene resin may have a meltingpoint of about 255-295 or 295-330 degrees F. In another example,ballistic sheets in a panel may be coated or impregnated with apolyethylene resin, and the polyethylene resin may have a melting pointof about 215-240 degrees F. During a manufacturing process to make aballistic resistant panel 100, the stack of ballistic sheets 1005 may beheated to a temperature near the melting point of the resin to causesoftening of the resin, and pressure may be applied to the stack ofballistic sheets to press adjacent ballistic sheets closer together.When the panel 100 is cooled, and the temperature of the resin isreduced, adjacent ballistic sheets (e.g. 25) may be left partially orfully bonded to each other.

When forming a ballistic panel 100 from one or more ballistic sheets(e.g. 25) containing one or more resins, a suitable processingtemperature for the panel can be dictated, at least partly, by the resintype and resin content (i.e. percent weight) of the ballistic sheets.Selecting a resin with a lower melting point may reduce a targetprocessing temperature for the panel 100, and selecting a resin with ahigher melting point may increase the target processing temperature forthe panel. The amount of partial or full bonding that occurs betweenadjacent ballistic sheets in the stack can be controlled, at least inpart, by resin selection, resin content, process temperature, andprocess pressure.

Commercially-Available Ballistic Sheets

Ballistic resistant sheets constructed from high performance fibers,such as fibers made of aramids, para-aramids, meta-aramids, polyolefins,or ultra-high-molecular-weight polyethylenes, are commercially availablefrom a variety of manufacturers. Several specific examples ofcommercially-available ballistic resistant sheets made of highperformance fibers are provided below. Ballistic resistant sheets arecommercially-available in many configurations, including uni-ply, 0/90x-ply, and 0/90/0/90 double x-ply configurations. Ballistic resistantsheeting material can be ordered in a wide variety of forms, includingtapes, rolls, sheets, structural sandwich panels, and preformed inserts,which can all be cut to size during a manufacturing process.

TechFiber, LLC, located in Arizona, manufactures a variety of ballisticresistant sheets made of aramid fibers that are sold under the trademarkK-FLEX. One version of K-FLEX is made with KEVLAR fibers having a denierof about 1000 and a pick count of about 18 picks per inch. Certainversions of K-FLEX can have a resin content of about 15-20%. Differentversions of K-FLEX may contain different resins. For instance, a firstversion of K-FLEX can include a resin (e.g. a polyethylene resin) with amelting temperature of about 215-240 degrees F., a second version ofK-FLEX can include a resin with a melting temperature of about 240-265degrees F., a third version of K-FLEX can include a resin with a meltingtemperature of about 265-295 degrees F., and a fourth version of K-FLEXcan include a resin with a melting temperature of about 295-340 degreesF. K-FLEX is available in uni-ply, 0/90 x-ply, and 0/90/0/90 doublex-ply configurations.

TechFiber, LLC also manufactures a variety of unidirectional ballisticresistant sheets made of aramid fibers that are sold under the trademarkT-FLEX. Certain versions of T-FLEX can have a resin content of about15-20% and can include aramid fibers such as TWARON fibers (e.g. modelnumber T765). Different versions of T-FLEX may contain different resins.For instance, a first version of T-FLEX can include a resin (e.g. apolyethylene resin) with a melting temperature of about 215-240 degreesF., a second version of T-FLEX can include a resin with a meltingtemperature of about 240-265 degrees F., a third version of T-FLEX caninclude a resin with a melting temperature of about 265-295 degrees F.,and a fourth version of T-FLEX can include a resin with a meltingtemperature of about 295-340 degrees F. T-FLEX is available in uni-ply,0/90 x-ply, and 0/90/0/90 double x-ply configurations.

Polystrand, Inc., located in Colorado, manufactures a variety ofunidirectional ballistic resistant sheets made of aramid fibers that aresold under the trademark THERMOBALLISTIC. One version of THERMOBALLISTICballistic resistant sheets are sold as product number TBA-8510 andinclude aramid fibers with a pick count of about 12.5 picks per inch.Other versions of THERMOBALLISTIC ballistic resistant sheets are sold asproduct numbers TBA-8510X and TBA-9010X and include aramid fibers (e.g.KEVLAR fibers) and have a 0/90 x-ply configuration. In certain versions,the resin content of the THEMROBALLISTIC ballistic resistant sheets canbe about 10-20% or 15-20%. Different versions of THERMOBALLISTICballistic resistant sheets may contain different resins. For instance, afirst version of THERMOBALLISTIC ballistic resistant sheets can includea resin with a melting temperature of about 225-255 degrees F., a secondversion of THERMOBALLISTIC ballistic resistant sheets can include aresin (e.g. a polypropylene resin) with a melting temperature of about255-295 degrees F., a third version of THERMOBALLISTIC ballisticresistant sheets can include a resin (e.g. a polypropylene resin) with amelting temperature of about 295-330 degrees F., a fourth version ofTHERMOBALLISTIC ballistic resistant sheets can include a resin with amelting temperature of about 330-355 degrees F., and a fifth version ofTHERMOBALLISTIC ballistic resistant sheets can include a resin with amelting temperature of about 355-375 degrees F. One version ofTHERMOBALLISTIC ballistic resistant sheets can include a polypropyleneresin. THERMOBALLISTIC ballistic resistant sheets are available inuni-ply, 0/90 x-ply, and 0/90/0/90 double x-ply configurations.

E. I. du Pont de Nemours and Company (DuPont), headquartered inDelaware, manufactures a ballistic resistant sheet material made ofultra-high-molecular-weight polyethylene fabric that is sold under thetrademark TENSYLON. A Material Data Safety Sheet was prepared on Feb. 2,2010 for a material sold under the tradename TENSYLON HTBD-09-A (Gen 2)by BAE Systems TENSYLON High Performance Materials. The Material SafetyData Sheet is identified as TENSYLON MSDS Number 1005, is publiclyavailable, and is hereby incorporated by reference in its entirety. Theballistic resistant sheets are marketed as being lightweight andcost-effective and boast low back face deformation, excellent flexuralmodulus, and superior multi-threat capability over other commerciallyavailable ballistic resistant sheets. The ballistic resistant sheetmaterial can be purchased on a roll and can be cut into ballisticresistant sheets having a size and shape dictated by an intendedapplication.

Honeywell International, Inc., headquartered in New Jersey, manufacturesa variety of ballistic resistant sheets made of aramid fibers that aresold under the trademarks GOLD SHIELD and GOLD FLEX. One version of GOLDSHIELD ballistic resistant sheets are sold under product number GN-2117and are available in 0/90 x-ply configurations and have an areal densityof about 3.2 ounces per square yard.

Barrday, Inc., headquartered in Cambridge, Ontario, manufactures avariety of ballistic resistant sheets made of para-aramid fibers thatare sold under the trademark BARRFLEX. One version of BARRFLEX ballisticresistant sheets is sold as product number U480 and is available in 0/90x-ply configurations. Each layer of the ballistic resistant sheet isindividually constructed with a thermoplastic film laminated to a topand bottom surface.

Teijin Limited, headquartered in the Netherlands, manufactures aballistic resistant sheet material made of ultra-high-molecular-weightpolyethylene fabric in a solvent-free process. The sheet material issold under the trademark ENDUMAX and is available with a thickness ofabout 55 micrometers.

Ply-Tech, Inc., located in New Braunfels, Tex. manufactures a variety ofballistic resistant sheets made of aramid fibers that are sold under thetrademark KM2 1000. One version of KM2 1000 is made of 1,000 denierKEVLAR KM2 brand yarn from DuPont and is a biaxial (i.e. 0/90 X-ply)ballistic resistant sheet 250 with a fabric weight (i.e. areal density)of about 5.7 ounces per square yard. The KM2 1000 0/90 X-ply ballisticresistant sheet 250 can include two uni-ply ballistic resistant sheets(e.g. 50, 55) bonded together with an adhesive resin. Each uni-plyballistic sheet (e.g. 50, 55) can include a plurality of KM2 brandfibers arranged unidirectionally to form a two-dimensional arrangementof fibers, and the sheets can be cross-plied to provide a 0/90 X-plyconfiguration. A polyethylene film can be applied over each uni-plyballistic resistant sheet prior to joining the sheets with adhesiveresin to form the 0/90 X-ply ballistic resistant sheet 250.

Vectorply Corporation, located in Phenix City, Ala. manufactures avariety of stitch-bonded multiaxial fabrics. Stitch-bonded multiaxialfabrics can include cross-plies of high-performance fabrics that arestitched together. In one example, a quad-axial stitch-bonded fabric caninclude four plies arranged at 0, 90, 45, and −45 degrees, respectivelyand bonded with tricot stitching. Each ply can be made of a plurality ofunilaterally arranged fibers, such as carbon fibers, Kevlar fibers, orUHMWPE fibers. The stitch style and density can alter the performance ofthe fabric. The stitch pattern can be, for example, chain, tricot, ormodified tricot. In a manufacturing process, needles can be mounted on astitch bar, which can simultaneously move vertically and horizontally toform a desired stitch pattern. Stitch yarn can be polyester, fiberglass,nylon, Nomex, aramid fiber, UHMWPE (e.g. Honeywell Spectra) fiber, orcarbon fiber.

Protective Cover

The stack of ballistic sheets 1005 can be encased in a protective cover1105. In one example, protective cover 1105 can be a waterproof cover,thereby producing a waterproof ballistic resistant panel. The waterproofcover 1105 can be adapted to prevent the ingress of liquid through thecover toward the ballistic sheets encased by the cover. FIG. 7 shows onestep of a manufacturing process for making a flexible ballisticresistant panel. In FIG. 7, a stack of ballistic sheets 1005 is beingpositioned within a waterproof cover 1105 prior to a vacuum baggingprocess. Preventing water ingress can be desirable, since moisture cannegatively affect the performance of the ballistic sheets. Inparticular, moisture can negatively affect tensile strength of certainfibers 11 (e.g. aramid fibers) within the ballistic sheets (e.g. 25),thereby resulting in the sheets being less effective at dissipatingimpact energy from a projectile.

The protective cover 1105 can be made from any suitable material suchas, for example, rubber, NYLON, RAYON, ripstop NYLON, CORDURA, polyvinylchloride (PVC), polyurethane, silicone elastomer, fluoropolymer, or anycombination thereof. The cover 1105 can be a coating that containspolyurethane, polyuria, or epoxy, such as a coating sold by RhinoLinings Corporation, located in San Diego, Calif. In another example,the waterproof cover 1105 can be made from any suitable waterproof ornon-waterproof material and coated with a waterproof material such as,for example, rubber, PVC, polyurethane, polytetrafluoroethylene,silicone elastomer, fluoropolymer, wax, or any combination thereof. Inone example, the cover 1105 can be made from NYLON coated with PVC. Inanother example, the cover can be made from NYLON coated withthermoplastic polyurethane. The cover 1105 can be made of any suitablematerial, such as about 50, 70, 200, 400, 600, 840, 1050, or 1680-denierNYLON coated with thermoplastic polyurethane. In yet another example,the cover can be made from 1000-denier CORDURA coated with thermoplasticpolyurethane.

In addition to being made of a waterproof material that protects theballistic sheets (e.g. 25) from water ingress, the protective cover 1105can also be made of a chemically-resistant material to protect theballistic sheets if the panel were ever exposed to acids or bases.Certain acids and bases can cause the tenacity of certain fibers, suchas aramid fibers, to degrade over time, where “tenacity” is a measure ofstrength of a fiber or yarn. It is therefore desirable, in certainapplications where exposure to chemicals is possible, for the cover 1105to be resistant to acids and bases to prevent the cover fromdeteriorating if ever exposed to acids or bases. Deterioration of thecover would be undesirable, since it would permit the acids and bases tobreach the cover material and reach the stack of ballistic sheets 1005inside the cover. To this end, the cover 1105 can be made of achemically-resistant material or can include a chemically-resistantcoating on an outer surface of the cover. For instance, the cover 1105can include a thermoplastic polymer coating on an outer surface of thecover. Examples of chemically-resistant thermoplastic polymers that canbe used to coat the cover include polypropylene, low-densitypolyethylene, medium-density polyethylene, high-density polyethylene,ultra-high-molecular-weight polyethylene, and polytetrafluoroethylene(e.g. TEFLON).

The protective cover 1105 can made of a flame-resistant orflame-retardant material. In one example, the cover 1105 can include aflame-resistant or flame-retardant material mixed with a base material.In another example, the cover 1105 can include a base material coatedwith a flame-resistant or flame-retardant material. In yet anotherexample, the cover can include a base material with a flame-resistant orflame-retardant material chemically bonded to the base material. Theflame-resistant or flame-retardant material can be a phenolic resin, aphenolic/epoxy composite, NOMEX, an organohalogen compound (e.g.chlorendic acid derivative, chlorinated paraffin, decabromodiphenylether, decabromodiphenyl ethane, brominated polystyrene, brominatedcarbonate oligomer, brominated epoxy oligomer, tetrabromophthalicanyhydride, tetrabromobisphenol A, or hexabromocyclododecane), anorganophosphorus compound (e.g. triphenyl phosphate, resorcinolbis(diphenylphosphate), bisphenol A diphenyl phosphate, tricresylphosphate, dimethyl methylphosphonate, aluminum diethyl phosphinate,brominated tris, chlorinated tris, ortetrekis(2-chlorethyl)dichloroisopentyldiphosphate, antimony trioxide,or sodium antimonite), or a mineral (e.g. aluminium hydroxide, magnesiumhydroxide, huntite, hydromagnesite, red phosphorus, or zinc borate).

The protective cover 1105, along with the stack of ballistic sheets1005, can be heated and subjected to a vacuum bagging process, therebypartially or fully bonding an inner surface of the cover to the stack ofballistic sheets 1005 encased by the cover. Full or partial bonding canprevent the stack of ballistic sheets 1005 from shifting within thecover 1105 during use, which can be important to ensure that ballisticperformance of the panel 100 is maintained. The cover 1105 can include atemperature sensitive adhesive or a layer of resin on an inner surface.The cover 1105 can be heated to promote full or partial bonding of theinner surface of the cover to the stack of ballistic sheets 1005 due tothe adhesive or resin. In one example, the cover can be made of amaterial that is coated with polyurethane, polypropylene, vinyl,polyethylene, or a combination thereof, on the inner surface the cover.Heating the cover 1105 to a temperature above the melting point of theadhesive or resin and then cooling the cover below the melting point ofthe adhesive or resin can result in bonding of the inner surface of thecover to the outer surface of the stack of ballistic sheets 1005.

In some examples, the protective cover 1105 can be made of ripstop NYLONcoated with polyurethane. The cover 1105 can be made of ripstop NYLONwith a polyurethane coating that is about 0.1-1.5, 0.1-0.75, 0.1-0.5, or0.25 mil thick. The cover 1105 can be made of 70-denier ripstop NYLONwith a polyurethane coating that is about 0.1-1.5, 0.1-0.75, 0.1-0.5, or0.25 mil thick. The polyurethane coating can be provided on an innersurface of the cover 1105. A durable water repellant finish can beprovided on an outer surface of the cover 1105. Suitable polyurethanecoated ripstop NYLON materials are commercially available under thetrademark X-PAC from Rockywoods Fabrics, LLC located in Loveland, Colo.

Vacuum Bagging

The stack of ballistic sheets 1005 can be vacuum bagged to remove airthat is present between adjacent sheets (e.g. 25), thereby compressingthe stack and reducing its thickness. During the vacuum bagging process,a stack of ballistic sheets 1005 are inserted into a vacuum bag, whichis then sealed, as shown in FIG. 9. A vacuum hose 1305 extending from avacuum pump is then connected to a vacuum port 1315 on the vacuum bag1310, and the vacuum pump is activated to effectively evacuate air fromthe vacuum bag through the vacuum hose. A breather layer 1320 can bepositioned between the panel 100 and the vacuum bag 1310 to ensureuniform evacuation of the vacuum bag. As air is evacuated from thevacuum bag 1310, the air pressure inside the bag decreases. Meanwhile,the ambient air pressure acting on the outside of the vacuum bag 1310remains at atmospheric pressure (e.g. ˜14.7 psi). The pressuredifferential between the air pressure inside and outside the bag issufficient to produce a suitable compressive force against the stack ofballistic sheets 1005 within the panel 100. The compressive force isapplied uniformly over the panel 100, thereby resulting in a panel withuniform or nearly uniform thickness.

In one example, the vacuum bag 1310 can be sized to accommodate oneballistic panel 100, as shown in FIG. 9. In another example, the vacuumbag 1310 can be sized to accommodate a plurality of ballistic panels100, as shown in FIG. 8. For instance, the vacuum bag can be sized toaccommodate two or more, 2-20, 4-12, or 6-10 ballistic panels. Vacuumbagging batches of ballistic panels 100 can be more efficient thanvacuum bagging individual panels, as shown in FIG. 9. Vacuum baggingbatches of panels 100 also allows for quality testing of at least onepanel per batch. Quality control testing of a panel 100 may involvedestructive testing, such as firing projectiles at the panel todetermine a V50 rating or a ballistic protection level. Therefore, it isdesirable to make two or more panels in an identical vacuum baggingprocess, where it can be assumed that the panels that are notdestructively tested will perform similarly to the panel that has beendestructively tested.

The vacuum bag used in the vacuum bagging process can be reusable, whichcan reduce consumables and decrease labor costs. The reusable vacuum bagcan be made from any suitable material, such as LEXAN, silicone rubber,TEFLON, fiberglass reinforced polyurethane, fiberglass reinforcedpolyester, or KEVLAR reinforced rubber.

Heating Process

During formation of the ballistic resistant panel 100, the stack ofballistic sheets 1005 can be heated in a heating process. Heating canpromote bonding (e.g. partial or full bonding) between adjacentballistic sheets. When adjacent ballistic sheets are fully (i.e.completely) bonded, it may be difficult or nearly impossible to separatethe sheets by hand, since former boundaries between adjacent sheets mayno longer exist due to various degrees of melting. When adjacent sheetsare partially bonded, it may still be possible to separate adjacentsheets by hand, depending on the extent of the partial bonding. Full orpartial bonding is desirable since it can enhance the panel's ability todissipate impact energy of a projectile that strikes the panel as theballistic sheets within the panel experience delamination. Duringdelamination, adjacent ballistic sheets that were partially or fullybonded prior to impact are separated (i.e. delaminated) in response tothe projectile entering the panel, and the energy required to separatethose ballistic sheets is dissipated from the projectile, therebyreducing the speed of the projectile and eventually stopping andcapturing the projectile. A panel 100 containing ballistic sheets thatare partially or fully bonded can more effectively dissipate impactenergy from a projectile than a panel that has no bonding and is simplya stack of ballistic sheets sewn together, such as the ballistic sheetsshown in the prior art bullet-proof vest in FIG. 6. The ballistic sheetsin FIG. 6 have no partial or full bonding between adjacent layers, whichis evident from the way the ballistic sheets can easily be fanned outafter an edge seam is undone. For this reason, the bullet-proof vest inFIG. 6 is unable to match the ballistic performance of the panels 100described herein.

In one example, heating of the stack of ballistic sheets 1005 can occurafter the stack has been vacuum bagged and while the stack is stillsealed within the vacuum bag 1310. In another example, the stack ofballistic sheets 1005 can be heated after vacuum bagging and after thestack has been removed from the vacuum bag 1310. In yet another example,heating can occur before the stack of ballistic sheets 1005 has beensubjected to a vacuum bagging process.

Heating can occur using any suitable heating equipment such as, forexample, a conventional oven, infrared oven, hydroclave, or autoclave.To ensure accurate temperature control throughout the heating process,the heating equipment can include a closed-loop controller, such as aproportional-integral-derivative (PID) controller. To avoid temperaturevariations throughout a heating chamber of the heating equipment, a fancan be installed and operated within the heating chamber. The fan cancirculate air throughout the heating chamber, thereby encouraging mixingof higher and lower temperature regions that may form within the heatingchamber (due, for example, to placement of a heating element), andattempting to produce a uniform (or nearly uniform) air temperatureadjacent to all outer surfaces of the panel 100 to ensure consistentbehavior of the resins in the ballistic sheets. In some examples, theheating chamber can be located within, or can be the same apparatus as,the pressure vessel described herein.

During the heating process, a process temperature can be selected based,at least in part, on a melting point of one or more resins that areincorporated into one or more of the ballistic sheets (e.g. 25) in thestack. For instance, if the stack includes a ballistic sheet containinga thermoplastic polymer resin (e.g. a polyethylene resin) with a meltingtemperature of about 215-240 degrees F., the process temperature can beincreased to about 200-240 degrees F. or beyond to promote softening ormelting of the resin in the ballistic sheet. Similarly, if the stackincludes a ballistic sheet containing a thermoplastic polymer resin(e.g. a polypropylene resin) with a melting temperature of about 255-295or 295-330 degrees F., the process temperature can be increased to about240-295 or about 280-330 degrees F. or beyond to promote softening ormelting of the resin in the ballistic sheet.

As noted herein, the panel 100 can include a stack of ballistic sheets1005 including at least a first plurality of ballistic sheets and asecond plurality of ballistic sheets. The first plurality of ballisticsheets can include a first thermoplastic polymer (i.e. first resin)having a first melting point, and the second plurality of ballisticsheets can include a second thermoplastic polymer (i.e. second resin)having a second melting point. The second melting point can be higherthan the first melting point. In one example, during the heatingprocess, it can be desirable to heat the panel to a temperature betweenthe first and second melting points, thereby causing melting of thefirst thermoplastic polymer and resulting in bonding (e.g. partial orfull bonding) of each sheet in the first plurality of ballistic sheetsto an adjacent sheet. Since the process temperature remains below thesecond melting point, the second thermoplastic polymer will not melt andthe second plurality of ballistic sheets may not undergo any bonding,thereby permitting flexibility of the panel to remain relatively highsince the ballistic sheets in the second plurality of ballistic sheetsare permitted to move relative to one another when the panel is flexed.

In one example, where the first melting point of the first resin in thefirst plurality of the ballistic sheets is about 215-240 degrees F. andthe second melting point of the second resin in the second plurality ofballistic sheets is about 295-330 degrees F., the process temperaturecan be about 250-275 or 265-275 degrees F. for at least 15 minutes orfor about 60 minutes or more. In another example, where the firstmelting point of the first resin in the first plurality of the ballisticsheets is about 215-240 degrees F. and the second melting point of thesecond resin in the second plurality of ballistic sheets is about255-295 degrees F., the process temperature can be about 200-240 degreesF. for at least 15 minutes or for about 60 minutes or more.

To promote partial or full bonding of adjacent ballistic sheets in thestack, the stack can be heated to a suitable temperature for a suitableduration. Suitable temperatures and durations may depend on the types ofresin or resins present in the one or more ballistic sheets in thestack. Examples of suitable process temperatures and durations for aheating process for any of the various stacks of ballistic sheetsdescribed herein can include: 200-550 degrees F. for at least 1 second;200-550 degrees F. for at least 5 minutes; 200-550 degrees F. for atleast 15 minutes; 200-550 degrees F. for at least 30 minutes; 200-550degrees F. for at least 60 minutes; 200-550 degrees F. for at least 90minutes; 200-550 degrees F. for at least 120 minutes; 200-550 degrees F.for at least 180 minutes; 200-550 degrees F. for at least 240 minutes;200-550 degrees F. for at least 480 minutes; 225-350 degrees F. for atleast 1 second; 225-350 degrees F. for at least 5 minutes; 225-350degrees F. for at least 15 minutes; 225-350 degrees F. for at least 30minutes; 225-350 degrees F. for at least 60 minutes; 225-350 degrees F.for at least 90 minutes; 225-350 degrees F. for at least 120 minutes;225-350 degrees F. for at least 180 minutes; 225-350 degrees F. for atleast 240 minutes; 250-350 degrees F. for at least 1 second; 250-350degrees F. for at least 5 minutes; 250-350 degrees F. for at least 15minutes; 250-350 degrees F. for at least 30 minutes; 250-350 degrees F.for at least 60 minutes; 250-350 degrees F. for at least 90 minutes;250-350 degrees F. for at least 120 minutes; 250-350 degrees F. for atleast 180 minutes; 250-350 degrees F. for at least 240 minutes; 250-300degrees F. for at least 1 second; 250-300 degrees F. for at least 5minutes; 250-300 degrees F. for at least 15 minutes; 250-350 degrees F.for at least 30 minutes; 250-300 degrees F. for at least 60 minutes;250-350 degrees F. for at least 90 minutes; 250-300 degrees F. for atleast 120 minutes; 250-300 degrees F. for at least 180 minutes; 250-300degrees F. for at least 240 minutes; 250-275 degrees F. for at least 1second; 250-275 degrees F. for at least 5 minutes; 250-275 degrees F.for at least 15 minutes; 250-275 degrees F. for at least 30 minutes;250-275 degrees F. for at least 60 minutes; 250-275 degrees F. for atleast 90 minutes; 250-275 degrees F. for at least 120 minutes; 250-275degrees F. for at least 180 minutes; 250-275 degrees F. for at least 240minutes; 265-275 degrees F. for at least 1 second; 265-275 degrees F.for at least 5 minutes; 250-275 degrees F. for at least 15 minutes;265-275 degrees F. for at least 30 minutes; 265-275 degrees F. for atleast 60 minutes; 265-275 degrees F. for at least 90 minutes; 265-275degrees F. for at least 120 minutes; 265-275 degrees F. for at least 180minutes; 265-275 degrees F. for at least 240 minutes; 225-250 degrees F.for at least 1 second; 225-250 degrees F. for at least 5 minutes;225-250 degrees F. for at least 15 minutes; 225-250 degrees F. for atleast 30 minutes; 225-250 degrees F. for at least 60 minutes; 225-250degrees F. for at least 90 minutes; 225-250 degrees F. for at least 120minutes; 225-250 degrees F. for at least 180 minutes; 225-250 degrees F.for at least 240 minutes; 200-240 degrees F. for at least 1 second;200-240 degrees F. for at least 5 minutes; 200-240 degrees F. for atleast 15 minutes; 200-240 degrees F. for at least 30 minutes; 200-240degrees F. for at least 60 minutes; 200-240 degrees F. for at least 90minutes; 200-240 degrees F. for at least 120 minutes; 200-240 degrees F.for at least 180 minutes; or 200-240 degrees F. for at least 240minutes.

For any of the above-mentioned process temperatures and durations for aheating process, the stack of ballistic sheets 1005 may be sealed withina vacuum bag 1310 during the heating process. In certain examples, avacuum hose 1305 extending from a vacuum pump can remain connected to avacuum port 1315 on the vacuum bag 1310 during the heating process,thereby providing a compressive force against the panel 100 during theheating process. This configuration can ensure good results even if thevacuum bag 1310 is not perfectly sealed due to, for example, minor leaksin the bag material or sealant.

Exposing the panel to a higher temperature during the heating processcan effectively reduce cycle times, which is desirable for massproduction. Due to the thickness of the panel and heat transferproperties of the panel, exposing the panel to a high temperature (e.g.500 degrees F.) for a relatively short duration may allow the innerportion of the panel to achieve a target temperature needed for bonding(e.g. 250-275 degrees F.) more quickly than if the heat source wasinitially set to the target temperature needed for bonding.

Applying Pressure

During formation of the ballistic resistant panel 100, pressure can beapplied to the stack of ballistic sheets 1005. Pressure can promotepartial or full bonding of adjacent ballistic sheets (e.g. 25) in thestack 1005. Pressure can be applied to the stack of ballistic sheets1005 using a press (e.g. mechanical pressure), autoclave (e.g. airpressure), hydroclave, bladder press, or other suitable device. In oneexample, pressure can be applied to the stack of ballistic sheets 1005during the heating process. In another example, pressure can be appliedto the stack of ballistic sheets prior to the heating process. In yetanother example, pressure can be applied to the stack of ballisticsheets after the heating process, but while the stack of ballisticsheets is still at an elevated temperature. If pressure is applied tothe stack of ballistic sheets, it can occur after the stack of ballisticsheets 1005 has been vacuum bagged and while the stack is still residinginside the vacuum bag 1310 and being heated. Alternately, pressure canbe applied to the stack of ballistic sheets 1005 after the stack hasbeen removed from the vacuum bag 1310 or before the stack is insertedinto the vacuum bag.

During a process involving both heat and pressure, a process temperaturecan be selected based on a melting point of one or more thermoplasticpolymers (i.e. resins) that are incorporated into one or more of theballistic sheets in the stack 1005. For instance, if the stack 1005includes a ballistic sheet (e.g. 25) containing a first resin with amelting temperature of about 215-240 degrees F., the process temperaturecan be increased to about 200-240 degrees F. or beyond to promotesoftening or melting of the first resin in the stack. Similarly, if thestack 1005 includes a ballistic sheet containing a second resin with amelting temperature near 255-295 or 295-330 degrees F., the processtemperature can be increased to about 240-295 or 280-330 degrees F. orbeyond to promote softening or melting of the second resin in the stack.

To promote partial or full bonding of adjacent ballistic sheets (e.g.25) in the stack 1005, a suitable pressure can be applied to the stackfor a suitable duration. Suitable pressures and durations may depend onthe types of resin or resins present in the one or more ballistic sheetsin the stack. Examples of suitable process pressures and durations forany of the various stacks of ballistic sheets 1005 described herein caninclude: 10-100 psi for at least 1 second, 10-100 psi for at least 1second; 10-100 psi for at least 5 minutes; 10-100 psi for at least 15minutes; 10-100 psi for at least 30 minutes; 10-100 psi for at least 60minutes; 10-100 psi for at least 90 minutes; 10-100 psi for at least 120minutes; 10-100 psi for at least 180 minutes; 10-100 psi for at least240 minutes; 50-75 psi for at least 1 second; 50-75 psi for at least 5minutes; 50-75 psi for at least 15 minutes; 50-75 psi for at least 30minutes; 50-75 psi for at least 60 minutes; 50-75 psi for at least 90minutes; 50-75 psi for at least 120 minutes; 50-75 psi for at least 180minutes; 50-75 psi for at least 240 minutes; 75-100 psi for at least 1second; 75-100 psi for at least 5 minutes; 75-100 psi for at least 15minutes; 75-100 psi for at least 30 minutes; 75-100 psi for at least 60minutes; 75-100 psi for at least 90 minutes; 75-100 psi for at least 120minutes; 75-100 psi for at least 180 minutes; 75-100 psi for at least240 minutes; at least 10 psi for at least 1 second; at least 10 psi forat least 5 minutes; at least 10 psi for at least 15 minutes; at least 10psi for at least 30 minutes; at least 10 psi for at least 60 minutes; atleast 10 psi for at least 90 minutes; at least 100 psi for at least 120minutes; at least 10 psi for at least 180 minutes; at least 10 psi forat least 240 minutes; at least 100 psi for at least 1 second; at least100 psi for at least 5 minutes; at least 100 psi for at least 15minutes; at least 100 psi for at least 30 minutes; at least 100 psi forat least 60 minutes; at least 100 psi for at least 90 minutes; at least100 psi for at least 120 minutes; at least 100 psi for at least 180minutes; or at least 100 psi for at least 240 minutes.

Lower pressures may be achievable with, for example, a manual press or asmall autoclave. In other examples, higher pressures can be applied tothe stack of ballistic sheets with, for example, an industrialautoclave, hydroclave, bladder press (e.g. made of KEVLAR reinforcedrubber), a pneumatic press, or a hydraulic press. To promote partial orfull bonding of adjacent ballistic sheets in the stack, a suitablepressure can be applied to the stack for a suitable duration or onlymomentarily. Suitable pressures and durations may depend on the types ofresin or resins present in the one or more ballistic sheets in thestack. Examples of suitable process pressures and durations for any ofthe various stacks of ballistic sheets described herein can include:100-500 psi for at least 1 second; 100-500 psi for at least 5 minutes;100-500 psi for at least 15 minutes; 100-500 psi for at least 30minutes; 100-500 psi for at least 60 minutes; 100-500 psi for at least90 minutes; 100-500 psi for at least 120 minutes; 100-500 psi for atleast 180 minutes; 100-500 psi for at least 240 minutes; 500-1,000 psifor at least 1 second; 500-1,000 psi for at least 5 minutes; 500-1,000psi for at least 15 minutes; 500-1,000 psi for at least 30 minutes;500-1,000 psi for at least 60 minutes; 500-1,000 psi for at least 90minutes; 500-1,000 psi for at least 120 minutes; 500-1,000 psi for atleast 180 minutes; 500-1,000 psi for at least 240 minutes; 1,000-2,500psi for at least 1 second; 1,000-2,500 psi for at least 5 minutes;1,000-2,500 psi for at least 15 minutes; 1,000-2,500 psi for at least 30minutes; 1,000-2,500 psi for at least 60 minutes; 1,000-2,500 psi for atleast 90 minutes; 1,000-2,500 psi for at least 120 minutes; 1,000-2,500psi for at least 180 minutes; 1,000-2,500 psi for at least 240 minutes;at least 2,500 psi for at least 1 second; at least 2,500 psi for atleast 5 minutes; at least 2,500 psi for at least 15 minutes; at least2,500 psi for at least 30 minutes; at least 2,500 psi for at least 60minutes; at least 2,500 psi for at least 90 minutes; at least 2,500 psifor at least 120 minutes; at least 2,500 psi for at least 180 minutes;or at least 2,500 psi for at least 240 minutes.

Combination of Heat and Pressure

If a process for manufacturing a ballistic panel 100 requires heat andpressure, heat and pressure can be applied simultaneously to reduce theoverall cycle time required to manufacture the panel. An autoclave canfacilitate these combined processes. An autoclave is a pressure vesselthat can be used to apply pressure and heat to one or more ballisticpanels 100 during a manufacturing process. If pressure is applied duringthe heating process, the process temperature can be modified to accountfor the effect that pressure has on the melting point of the one or moreresins that are incorporated in one or more of the ballistic sheets inthe stack 1005. For instance, if the melting point of the resinincreases as pressure increases, the target process temperature for theheating process can be increased when the heating process occurs inconjunction with the pressure process to ensure melting of the resin.

3-Dimensional Forming Process

During a forming process, a mold can be used to transform a flatballistic resistant panel 100 into any suitable 3-dimensional shape. Inone example, the forming process can occur concurrently with the vacuumbagging process. In another example, pressure, such as air pressurewithin an autoclave, can be used to form the ballistic resistant panelinto any suitable 3-dimensional shape while the panel 100 is still inthe vacuum bag 1310. In yet another example, pressure, such as airpressure within an autoclave, and heat can be used to form the ballisticresistant panel 100 into any suitable 3-dimensional shape while thepanel 100 is still in the vacuum bag 1310. In still another example, thepanel 100 may be inserted into a mold while still at an elevatedtemperature following the heating process, and a press can be used toconform the panel to the shape of the mold.

Heat Sealing

As discussed above, the stack of ballistic sheets 1005 can be encased ina protective cover 1105. The outer perimeter of the cover 1105 can beheat-sealed to prevent water ingress. Heat sealing is a process whereone material is joined to another material (e.g. one thermoplastic isjoined to another thermoplastic) using heat and pressure. During theheat sealing process, a heated die or sealing bar can apply heat andpressure to a specific contact area or path to seal or join twomaterials together. When heat-sealing the perimeter of the cover, thepresence of a thermoplastic material proximate the contact area canpromote sealing in the presence of heat and pressure. In one example,the cover 1105 can include thermoplastic polyurethane proximate thecontact area to permit heat sealing. The cover 1105 can be made of afirst portion and a second portion, and the heat sealing process can beused to join the first portion to the second portion, therebyencapsulating the stack of ballistic sheets 1005 in a waterproofenclosure.

Cooling

After the stack of ballistic sheets 1005 has been heated to apredetermined temperature for a predetermined duration, the stack can becooled. In one example, the cooling process can occur while the stack ofballistic sheets is outside of the vacuum bag 1310. In another example,the cooling process can occur while the stack of ballistic sheets 1005is inside the vacuum bag with vacuum applied. During the coolingprocess, the temperature of the stack of ballistic sheets 1005 can bereduced from the predetermined temperature to about room temperature.Cooling can occur through natural convection, forced convection, liquidcooling, or any other suitable cooling process. If liquid cooling isemployed, a suitable spray cooling process can be employed. Alternately,the stack of ballistic sheets 1005 encased in the waterproof cover 1105can be submerged in a water bath. The water bath can be connected to aheat exchanger and a circulating pump to increase the rate of cooling.

Break-in Process

For certain applications, it is desirable to manufacture a ballisticpanel 100 that is relatively flexible. For instance, when the panel isintended for use in a personal garment, such as a bullet-proof vest 30as shown in FIG. 5, it can be desirable to use a flexible panel 100 thatprovides the wearer greater mobility. Panels that are relativelyflexible are generally referred to as “soft armor,” whereas panels thatare relatively rigid, such as a steel or ceramic plate 32 shown in FIG.5 are generally referred to as “hard armor.” To further improve theflexibility of the soft armor panels described herein, the panels can besubjected to a break-in process. The break-in process can beaccomplished by hand or by mechanical devices. Mechanical devices can beused to speed the break-in process and to provide greater consistencyamong a series of panels, thereby improving quality control and ensuringconsistent panel performance. In one example, a series of rollers can beconfigured to receive the flexible panel 100. As the panel 100 passesthrough a first set of rollers, the panel may be deformed in a firstdirection to transform the nearly flat panel to a curved panel. Due tothe resilience of the stack of ballistic sheets, the panel 100 mayreturn to a nearly flat panel shortly after exiting the first set ofrollers. The panel 100 may then pass through a second set of rollersconfigured to deform the panel in a second direction that is oppositethe first direction. Once again, due to the resilience of the stack ofballistic sheets, the panel may return to a nearly flat panel shortlyafter exiting the second set of rollers. To further enhance theflexibility of the panel, the panel may be fed through the first andsecond rollers one or more additional times.

Methods or Cutting Ballistic Sheets

The intended use of the ballistic panel 100 will affect the size andshape of the panel, and the size and shape of the panel will dictate thegeometry of a pattern (e.g. two-dimensional pattern) that is cut fromthe ballistic sheet 25. The intended use of the panel will also dictatehow many ballistic sheets should be included in the panel to satisfycertain performance standards, such as those set forth in NIJStandard-0101.06.

In one example, ballistic sheets 25 can be cut from large rolls ofballistic sheet material. Due to the size of the sheets, it is commonfor one or more patterns be cut from a single ballistic sheet. Thepatterns can be arranged on the ballistic sheet to minimize the amountof ballistic sheet material that is wasted. In one example, a computerprogram can be used to determine an arrangement of patterns thatminimizes the amount of wasted ballistic sheet material.

The ballistic sheets 25 can be cut on a cutting table, such as a modelM9000 manufactured by Eastman Machine Company of Buffalo, N.Y. The topsurface of the cutting table can include a plurality of holes. Thecutting table can be connected to a vacuum pump that applies suction toa lower side of the top surface, thereby drawing air through theplurality of holes and creating suction proximate the top surface of thecutting table. During cutting, the ballistic material can be placed onthe cutting table. The suction can assist in preventing movement of theballistic sheet relative to the cutting table during the cuttingprocess, which can improve cutting performance and precision and reducethe quantity of wasted material. Employing a cutting table with a vacuumsystem can reduce fraying of fibers at a cutting location by avoidingunwanted movement of the ballistic sheet during the cutting process.

The top surface of the cutting table can be made of any suitablematerial. In one example, the top surface of the cutting table can bemade of POREX, a porous polymer material. POREX can be costly to replaceif damaged by a cutting process or through misuse. A less expensivepolymer sheet can be used to cover and protect the POREX. For instance,a LEXAN sheet can be used to cover and protect the POREX surface. TheLEXAN sheet can include a plurality of holes that permit air to passthrough the sheet and allow suction to be created proximate a topsurface of the LEXAN sheet. If the LEXAN sheet is damaged during acutting process, it can be replaced at a much lower cost than POREX. Dueto its machinability, the LEXAN sheet can permit an operator to easilydrill or create any suitable hole pattern in the LEXAN sheet. Thenumber, size, or configuration of the plurality holes can vary dependingon the pattern to be cut from the ballistic sheet. This provides theoperator with additional process flexibility that can enhance cuttingperformance (e.g. the LEXAN sheet can be modified to intentionally coverand obstruct certain pores in the POREX, thereby increasing the suctionproximate the remaining unobstructed pores). If the operator is cuttingtwo patterns on the same cutting table in a single day, the operator canhave two LEXAN sheets that are each optimized for cutting one of the twopatterns. For instance, a first LEXAN sheet can have a number, size, andconfiguration of holes that is optimized for a first pattern, and asecond LEXAN sheet can have a number, size, and configuration of holesthat is optimized for a second pattern.

Methods for Cutting a Plurality of Ballistic Sheets

To increase efficiency, it can be desirable to cut a pattern from two ormore ballistic sheets simultaneously. This can be accomplished bystacking two or more ballistic sheets prior to cutting the sheets.Cutting can be accomplished on a cutting table with any suitable cuttingtool, such as a laser, blade, rotary knife, or die cutter. In oneexample the cutting tool can be a drag knife mounted to a computercontrolled gantry. When a drag knife is used, a downward cutting forcefrom the drag knife is applied against the stack of ballistic sheetsand, in turn, against the top surface of the cutting table (or LEXANsheet covering the cutting table).

If two or more types of ballistic sheets are being cut simultaneously ina stack, the resulting cut quality of each ballistic sheet can depend onthe arrangement of the ballistic sheets within the stack. Certain typesof ballistic sheets that are less stiff exhibit poor cut quality ifplaced on top of the stack. For instance, ballistic sheets that are lessstiff may suffer poor cut quality, such as fraying along their edges orfibers pulling from the sheets by the drag knife, which can compromisethe ballistic performance of the sheets.

However, it has been discovered through experimentation that boundingballistic sheets that are less stiff with ballistic sheets that arestiffer can provide better cut quality along an edge of the less stiffballistic sheet and produce significantly less fraying or pulling offibers at the edge of the less stiff ballistic sheet. In one example, agrouping of one or more ballistic sheets that are less stiff can bebounded on a top surface by a grouping of one or more ballistic sheetsthat are stiffer. Specifically, a stack of ballistic sheets that issuitable for cutting on a cutting table can include a first grouping ofone or more stiffer ballistic sheets on top of a second grouping of oneor more less stiff ballistic sheets. In another example, a grouping ofone or more ballistic sheets that are less stiff can be bounded on a topsurface and a bottom surface by grouping of one or more ballistic sheetsthat are stiffer. Specifically, a stack of ballistic sheets that issuitable for cutting on a cutting table can include a first grouping ofone or more stiffer ballistic sheets, a second grouping of one or moreless stiff ballistic sheets, and a third grouping of one or more stifferballistic sheets.

The flexibility of commercially available ballistic sheets varies. Inrelative terms, K-FLEX ballistic sheets can be less stiff thanTHERMOBALLISTIC ballistic sheets. K-FLEX ballistic sheets can have astiffness similar to fabric used for garments, whereas THERMOBALLISTICballistic sheets can have a stiffness similar to a paper business card.When cutting one or more K-FLEX ballistic sheets, cutting performancecan be enhanced by grouping the one or more K-FLEX ballistic sheets withone or more THERMOBALLISTIC ballistic sheets, where the one or moreTHERMOBALLISTIC ballistic sheets are either on a top side only or onboth a top and bottom side of the one or more K-FLEX ballistic sheets.These groupings of ballistic sheets can provide cleaner cuts with lessfraying along edges of the K-FLEX ballistic sheets. Reducing frayingalong edges of the cut sheets can help ensure that the performance ofthe sheets is not degraded and, ultimately, that the resulting ballisticpanel 100 performs as intended.

Examples of stacks of ballistic sheets suitable for cutting on a cuttingtable include the following configurations, where the first listedgrouping in each stack is in closest proximity to the top surface of thecutting table, and the last listed grouping in each stack is farthestfrom the top surface of the cutting table: 1-6 THERMOBALLISTIC 0/90x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-6THERMOBALLISTIC 0/90 x-ply ballistic sheets; 1-5 THERMOBALLISTIC 0/90x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-5THERMOBALLISTIC 0/90 x-ply ballistic sheets; 1-4 THERMOBALLISTIC 0/90x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-4THERMOBALLISTIC 0/90 x-ply ballistic sheets; 1-3 THERMOBALLISTIC 0/90x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-3THERMOBALLISTIC 0/90 x-ply ballistic sheets; 1-2 THERMOBALLISTIC 0/90x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-2THERMOBALLISTIC 0/90 x-ply ballistic sheets; 1 THERMOBALLISTIC 0/90x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1THERMOBALLISTIC 0/90 x-ply ballistic sheets; 6 THERMOBALLISTIC 0/90x-ply ballistic sheets, 10 K-FLEX 0/90 x-ply ballistic sheets, 6THERMOBALLISTIC 0/90 x-ply ballistic sheets; 6 THERMOBALLISTIC 0/90x-ply ballistic sheets, 8 K-FLEX 0/90 x-ply ballistic sheets, 6THERMOBALLISTIC 0/90 x-ply ballistic sheets; or 1 or moreTHERMOBALLISTIC 0/90 x-ply ballistic sheets, 1 or more K-FLEX 0/90 x-plyballistic sheets, 1 or more THERMOBALLISTIC 0/90 x-ply ballistic sheets.

Additional examples of stacks of ballistic sheets suitable for cuttingon a cutting table are provided below, where a first plurality ofballistic sheets (e.g. one or more K-FLEX 0/90 x-ply ballistic sheets)are bounded by a second plurality of ballistic sheets (e.g. one or moreTHERMOBALLISTIC 0/90 x-ply ballistic sheets). In the following examples,the first listed grouping in each stack is in closest proximity to thetop surface of the cutting table: 1-6 K-FLEX 0/90 x-ply ballisticsheets, 1-6 THERMOBALLISTIC 0/90 x-ply ballistic sheets; 1-4 K-FLEX 0/90x-ply ballistic sheets, 1-6 THERMOBALLISTIC 0/90 x-ply ballistic sheets;2-4 K-FLEX 0/90 x-ply ballistic sheets, 3-6 THERMOBALLISTIC 0/90 x-plyballistic sheets; 3-4 K-FLEX 0/90 x-ply ballistic sheets; 4-6THERMOBALLISTIC 0/90 x-ply ballistic sheets; 3 K-FLEX 0/90 x-plyballistic sheets, 6 THERMOBALLISTIC 0/90 x-ply ballistic sheets; 4K-FLEX 0/90 x-ply ballistic sheets, 6 THERMOBALLISTIC 0/90 x-plyballistic sheets.

Homogeneous or Non-Homogeneous Stack

In one example, the ballistic sheets can be arranged in a homogeneousstack, where all ballistic sheets in the stack are made from the sametype of ballistic sheet material. In other examples, any of the otherssuitable types of ballistic sheets (e.g. sheets made of aramid or glassfibers, sheets made of ceramic, or sheets made of metal) can beinterspersed in the stack of ballistic sheet material to improve theballistic performance of the stack. In another example, a sheet of filmadhesive, such as a sheet of film adhesive available from Collano AG,located in Germany, can be interspersed in the stack of ballistic sheetsto alter the ballistic performance of the stack. In particular, a sheetof adhesive film can be incorporated within the stack near a strike faceside of the stack to improve stab resistance of the panel. A sheet ofadhesive film can be incorporated within the stack near a wear face sideof the stack to reduce back face deformation of the panel after beingstruck by a projectile.

Panels Constructed from X-Ply Ballistic Sheets

Two uni-ply ballistic sheets can be bonded together to produce aconfiguration known as x-ply. Examples of suitable stacks of x-plyballistic sheets 1005 for a flexible ballistic resistant panel 100 caninclude a first plurality of x-ply ballistic sheets 1020 containing afirst resin with a first melting temperature and a second plurality ofx-ply ballistic sheets 1025 containing a second resin with a secondmelting temperature (see, e.g. FIGS. 11 and 12). The second meltingtemperature can be higher than the first melting temperature. Examplesinclude: 1-10 0/90 x-ply ballistic sheets containing a first resin and1-10 0/90 x-ply ballistic sheets containing a second resin; 4-10 0/90x-ply ballistic sheets containing a first resin and 4-10 0/90 x-plyballistic sheets containing a second resin; 6-10 0/90 x-ply ballisticsheets containing a first resin and 6-10 0/90 x-ply ballistic sheetscontaining a second resin; 10-20 0/90 x-ply ballistic sheets containinga first resin and 10-20 0/90 x-ply ballistic sheets containing a secondresin; 20-30 0/90 x-ply ballistic sheets containing a first resin and20-30 0/90 x-ply ballistic sheets containing a second resin.

Examples of suitable stacks of x-ply ballistic sheets 1005 containingaramid fibers can include a first plurality of x-ply ballistic sheets1020 containing aramid fibers and a first resin with a first meltingtemperature and a second plurality of x-ply ballistic sheets 1025containing aramid fibers and a second resin with a second meltingtemperature (see, e.g. FIGS. 11 and 12). The second melting temperaturecan be higher than the first melting temperature. Examples include: 1-100/90 x-ply ballistic sheets containing a first resin and 1-10 0/90 x-plyballistic sheets containing a second resin; 4-10 0/90 x-ply ballisticsheets containing a first resin and 4-10 0/90 x-ply ballistic sheetscontaining a second resin; 6-10 0/90 x-ply ballistic sheets containing afirst resin and 6-10 0/90 x-ply ballistic sheets containing a secondresin; 10-20 0/90 x-ply ballistic sheets containing a first resin and10-20 0/90 x-ply ballistic sheets containing a second resin; 20-30 0/90x-ply ballistic sheets containing a first resin and 20-30 0/90 x-plyballistic sheets containing a second resin.

Examples of suitable stacks of x-ply ballistic sheets 1005 for aflexible ballistic panel 100 can include a first plurality of x-plyballistic sheets 1020 containing a polyethylene resin with a meltingtemperature of about 215-240 degrees F. and a second plurality of x-plyballistic sheets 1025 containing a polypropylene resin with a meltingtemperature of about 255-295 or 295-330 F (see, e.g. FIGS. 11 and 12).Examples include: 1-10 0/90 x-ply ballistic sheets containing apolyethylene resin and 1-10 0/90 x-ply ballistic sheets containing apolypropylene resin; 4-10 0/90 x-ply ballistic sheets containing apolyethylene resin and 4-10 0/90 x-ply ballistic sheets containing apolypropylene resin; 6-10 0/90 x-ply ballistic sheets containing apolyethylene resin and 6-10 0/90 x-ply ballistic sheets containing apolypropylene resin; 10-20 0/90 x-ply ballistic sheets containing apolyethylene resin and 10-20 0/90 x-ply ballistic sheets containing apolypropylene resin; 20-30 0/90 x-ply ballistic sheets containing apolyethylene resin and 20-30 0/90 x-ply ballistic sheets containing apolypropylene resin.

Examples of suitable stacks of x-ply ballistic sheets 1005 for aflexible ballistic panel 100 can include a first plurality ofTHERMOBALLISTIC ballistic sheets 1025 arranged in a stack having a topsurface and a bottom surface and bounded on the top surface by a firstplurality of K-FLEX ballistic sheets 1020 and bounded on the bottomsurface by a second plurality of K-FLEX ballistic sheets 1030, as shownin FIG. 11. Examples include: 1-10 K-FLEX 0/90 x-ply ballistic sheets,1-10 THERMOBALLISTIC 0/90 x-ply ballistic sheets, 1-10 K-FLEX 0/90 x-plyballistic sheets; 4-10 K-FLEX 0/90 x-ply ballistic sheets, 4-10THERMOBALLISTIC 0/90 x-ply ballistic sheets, 4-10 K-FLEX 0/90 x-plyballistic sheets; 6-10 K-FLEX 0/90 x-ply ballistic sheets, 6-10THERMOBALLISTIC 0/90 x-ply ballistic sheets, 6-10 K-FLEX 0/90 x-plyballistic sheets; 8 K-FLEX 0/90 x-ply ballistic sheets, 10THERMOBALLISTIC 0/90 x-ply ballistic sheets, 8 K-FLEX 0/90 x-plyballistic sheets; 6 K-FLEX 0/90 x-ply ballistic sheets, 8THERMOBALLISTIC 0/90 x-ply ballistic sheets, 6 K-FLEX 0/90 x-plyballistic sheets; 5 K-FLEX 0/90 x-ply ballistic sheets, 8THERMOBALLISTIC 0/90 x-ply ballistic sheets, 5 K-FLEX 0/90 x-plyballistic sheets; 4 K-FLEX 0/90 x-ply ballistic sheets, 8THERMOBALLISTIC 0/90 x-ply ballistic sheets, 4 K-FLEX 0/90 x-plyballistic sheets; 10-20 K-FLEX 0/90 x-ply ballistic sheets, 10-20THERMOBALLISTIC 0/90 x-ply ballistic sheets, 10-20 K-FLEX 0/90 x-plyballistic sheets; or 20-30 K-FLEX 0/90 x-ply ballistic sheets, 20-30THERMOBALLISTIC 0/90 x-ply ballistic sheets, 20-30 K-FLEX 0/90 x-plyballistic sheets.

Examples of suitable stacks of x-ply ballistic sheets 1005 for aflexible ballistic panel 100 can include a first plurality of K-FLEXballistic sheets 1025 arranged in a stack having a top surface and abottom surface and bounded on the top surface by a first plurality ofTHERMOBALLISTIC ballistic sheets 1020 and bounded on the bottom surfaceby a second plurality of THERMOBALLISTIC ballistic sheets 1030, as shownin FIG. 12. Suitable examples include: 1-10 THERMOBALLISTIC 0/90 x-plyballistic sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-10THERMOBALLISTIC 0/90 x-ply ballistic sheets; 4-10 THERMOBALLISTIC 0/90x-ply ballistic sheets, 4-10 K-FLEX 0/90 x-ply ballistic sheets, 4-10THERMOBALLISTIC 0/90 x-ply ballistic sheets; 6-10 THERMOBALLISTIC 0/90x-ply ballistic sheets, 6-10 K-FLEX 0/90 x-ply ballistic sheets, 6-10THERMOBALLISTIC 0/90 x-ply ballistic sheets; 8 THERMOBALLISTIC 0/90x-ply ballistic sheets, 10 K-FLEX 0/90 x-ply ballistic sheets, 8THERMOBALLISTIC 0/90 x-ply ballistic sheets; 6 THERMOBALLISTIC 0/90x-ply ballistic sheets, 8 THERMOBALLISTIC 0/90 x-ply ballistic sheets, 6THERMOBALLISTIC 0/90 x-ply ballistic sheets; 5 THERMOBALLISTIC 0/90x-ply ballistic sheets, 8 K-FLEX 0/90 x-ply ballistic sheets, 5THERMOBALLISTIC 0/90 x-ply ballistic sheets; 4 THERMOBALLISTIC 0/90x-ply ballistic sheets, 8 K-FLEX 0/90 x-ply ballistic sheets, 4THERMOBALLISTIC 0/90 x-ply ballistic sheets; 6 THERMOBALLISTIC 0/90x-ply ballistic sheets, 6 K-FLEX 0/90 x-ply ballistic sheets, 6THERMOBALLISTIC 0/90 x-ply ballistic sheets; 10-20 THERMOBALLISTIC 0/90x-ply ballistic sheets, 10-20 K-FLEX 0/90 x-ply ballistic sheets, 10-20THERMOBALLISTIC 0/90 x-ply ballistic sheets, or 20-30 THERMOBALLISTIC0/90 x-ply ballistic sheets, 20-30 K-FLEX 0/90 x-ply ballistic sheets,20-30 THERMOBALLISTIC 0/90 x-ply ballistic sheets.

Examples of suitable stacks of x-ply ballistic sheets 1005 for aballistic panel 100 can include a grouping of 1-10, 4-10, 6-10, 10-20,or 20-30 x-ply ballistic sheets 1005 made of fibers (such as, forexample, aramid fibers or UHMWPE fibers), as shown in FIG. 10. Examplesof suitable stacks of x-ply ballistic sheets 1005 for a ballistic panel100 can include a grouping of 1-10, 4-10, 6-10, 10-20, or 20-30THERMOBALLISTIC 0/90 x-ply ballistic sheets. Other examples of suitablestacks 1005 of x-ply ballistic sheets for a ballistic panel 100 caninclude a grouping of 1-10, 4-10, 6-10, 10-20 or 20-30 K-FLEX 0/90 x-plyballistic sheets.

Panels Constructed from Uni-Ply Ballistic Sheets

Examples of suitable stacks of uni-ply ballistic sheets 1005 for aflexible ballistic resistant panel 100 can include a first plurality ofuni-ply ballistic sheets 1020 containing a first resin with a firstmelting temperature and a second plurality of uni-ply ballistic sheets1025 containing a second resin with a second melting temperature (see,e.g. FIGS. 11 and 12). The second melting temperature can be higher thanthe first melting temperature. Examples include: 1-10 0/90 uni-plyballistic sheets containing a first resin and 1-10 0/90 uni-plyballistic sheets containing a second resin; 4-10 0/90 uni-ply ballisticsheets containing a first resin and 4-10 0/90 uni-ply ballistic sheetscontaining a second resin; 6-10 0/90 uni-ply ballistic sheets containinga first resin and 6-10 0/90 uni-ply ballistic sheets containing a secondresin; 10-20 0/90 uni-ply ballistic sheets containing a first resin and10-20 0/90 uni-ply ballistic sheets containing a second resin; 20-300/90 uni-ply ballistic sheets containing a first resin and 20-30 0/90uni-ply ballistic sheets containing a second resin.

Examples of suitable stacks of uni-ply ballistic sheets containingaramid fibers can include a first plurality of uni-ply ballistic sheets1020 containing aramid fibers and a first resin with a first meltingtemperature and a second plurality of uni-ply ballistic sheets 1025containing aramid fibers and a second resin with a second meltingtemperature (see, e.g. FIGS. 11 and 12). The second melting temperaturecan be higher than the first melting temperature. Examples include: 1-10uni-ply ballistic sheets containing a first resin and 1-10 uni-plyballistic sheets containing a second resin; 8-20 uni-ply ballisticsheets containing a first resin and 8-20 uni-ply ballistic sheetscontaining a second resin; 12-20 uni-ply ballistic sheets containing afirst resin and 12-20 uni-ply ballistic sheets containing a secondresin; 20-40 uni-ply ballistic sheets containing a first resin and 20-40uni-ply ballistic sheets containing a second resin; 40-60 uni-plyballistic sheets containing a first resin and 40-60 uni-ply ballisticsheets containing a second resin.

Examples of suitable stacks of uni-ply ballistic sheets 1005 forflexible ballistic resistant panels 100 can include a first plurality ofuni-ply ballistic sheets 1020 containing a polyethylene resin with amelting temperature of about 215-240 degrees F. and a second pluralityof uni-ply ballistic sheets 1025 containing a polypropylene resin with amelting temperature of about 255-295 or 295-330 F (see, e.g. FIGS. 11and 12). Examples include: 1-10 uni-ply ballistic sheets containing apolyethylene resin and 1-10 0/90 uni-ply ballistic sheets containing apolypropylene resin; 8-20 uni-ply ballistic sheets containing apolyethylene resin and 8-20 uni-ply ballistic sheets containing apolypropylene resin; 12-20 uni-ply ballistic sheets containing apolyethylene resin and 12-20 uni-ply ballistic sheets containing apolypropylene resin; 20-40 uni-ply ballistic sheets containing apolyethylene resin and 20-40 uni-ply ballistic sheets containing apolypropylene resin; 40-60 uni-ply ballistic sheets containing apolyethylene resin and 40-60 uni-ply ballistic sheets containing apolypropylene resin.

Examples of suitable stacks of uni-ply ballistic sheets 1005 for aflexible ballistic resistant panel 100 can include a first plurality ofTHERMOBALLISTIC ballistic sheets 1025 arranged in a stack having a topsurface and a bottom surface and bounded on the top surface by a firstplurality of K-FLEX ballistic sheets 1020 and bounded on the bottomsurface by a second plurality of K-FLEX ballistic sheets 1030, as shownin FIG. 11. Examples include: 2-20 K-FLEX uni-ply ballistic sheets, 2-20THERMOBALLISTIC uni-ply ballistic sheets, 2-20 K-FLEX uni-ply ballisticsheets; 8-20 K-FLEX uni-ply ballistic sheets, 8-20 THERMOBALLISTICuni-ply ballistic sheets, 8-20 K-FLEX uni-ply ballistic sheets; 12-20K-FLEX uni-ply ballistic sheets, 12-20 THERMOBALLISTIC uni-ply ballisticsheets, 12-20 K-FLEX uni-ply ballistic sheets; 16 K-FLEX uni-plyballistic sheets, 20 THERMOBALLISTIC uni-ply ballistic sheets, 16 K-FLEXuni-ply ballistic sheets; 12 K-FLEX uni-ply ballistic sheets, 16THERMOBALLISTIC uni-ply ballistic sheets, 12 K-FLEX uni-ply ballisticsheets; 10 K-FLEX uni-ply ballistic sheets, 16 THERMOBALLISTIC uni-plyballistic sheets, 10 K-FLEX uni-ply ballistic sheets; 8 K-FLEX uni-plyballistic sheets, 16 THERMOBALLISTIC uni-ply ballistic sheets, 8 K-FLEXuni-ply ballistic sheets; 20-40 K-FLEX uni-ply ballistic sheets, 20-40THERMOBALLISTIC uni-ply ballistic sheets, 20-40 K-FLEX uni-ply ballisticsheets; or 40-60 K-FLEX uni-ply ballistic sheets, 40-60 THERMOBALLISTICuni-ply ballistic sheets, 40-60 K-FLEX uni-ply ballistic sheets. In thestacks listed above, adjacent unidirectional ballistic sheets can beoriented to simulate 0/90 x-ply. For instance, in a stack of four sheetsof uni-ply, a first sheet can be oriented at 0 degrees, a second sheetcan be oriented at 90 degrees, a third sheet can be oriented at 0degrees, and a fourth sheet can be oriented at 90 degrees.

Examples of suitable stacks of uni-ply ballistic sheets 1005 can includea first plurality of K-FLEX ballistic sheets 1025 arranged in a stackhaving a top surface and a bottom surface and bounded on the top surfaceby a first plurality of THERMOBALLISTIC ballistic sheets 1020 andbounded on the bottom surface by a second plurality of THERMOBALLISTICballistic sheets 1030, as shown in FIG. 12. Suitable examples include:2-20 THERMOBALLISTIC uni-ply ballistic sheets, 2-20 K-FLEX uni-plyballistic sheets, 2-20 THERMOBALLISTIC uni-ply ballistic sheets; 8-20THERMOBALLISTIC uni-ply ballistic sheets, 8-20 K-FLEX uni-ply ballisticsheets, 8-20 THERMOBALLISTIC uni-ply ballistic sheets; 12-20THERMOBALLISTIC uni-ply ballistic sheets, 12-20 K-FLEX uni-ply ballisticsheets, 12-20 THERMOBALLISTIC uni-ply ballistic sheets; 16THERMOBALLISTIC uni-ply ballistic sheets, 20 K-FLEX uni-ply ballisticsheets, 16 THERMOBALLISTIC uni-ply ballistic sheets; 12 THERMOBALLISTICuni-ply ballistic sheets, 16 K-FLEX uni-ply ballistic sheets, 12THERMOBALLISTIC uni-ply ballistic sheets; 10 THERMOBALLISTIC uni-plyballistic sheets, 16 K-FLEX uni-ply ballistic sheets, 10 THERMOBALLISTICuni-ply ballistic sheets; 8 THERMOBALLISTIC uni-ply ballistic sheets, 16K-FLEX uni-ply ballistic sheets, 8 THERMOBALLISTIC uni-ply ballisticsheets; 20-40 THERMOBALLISTIC uni-ply ballistic sheets, 20-40 K-FLEXuni-ply ballistic sheets, 20-40 THERMOBALLISTIC uni-ply ballisticsheets; or 40-60 THERMOBALLISTIC uni-ply ballistic sheets, 40-60 K-FLEXuni-ply ballistic sheets, 40-60 THERMOBALLISTIC uni-ply ballisticsheets. In the stacks listed above, adjacent unidirectional ballisticsheets can be oriented to simulate 0/90 x-ply. For instance, in a stackof four sheets of uni-ply, a first sheet can be oriented at 0 degrees, asecond sheet can be oriented at 90 degrees, a third sheet can beoriented at 0 degrees, and a fourth sheet can be oriented at 90 degrees.

Examples of suitable stacks of unidirectional ballistic sheets 1005 fora flexible ballistic resistant panel 100 can include a grouping of 2-20,8-20, 12-20, 20-40, or 40-60 unidirectional ballistic sheets made offibers such as, for example, aramid or UHMWPE fibers. Examples ofsuitable stacks of unidirectional ballistic sheets 1005 for a ballisticpanel 100 can include a grouping of 2-20, 8-20, 12-20, 20-40, or 40-60unidirectional THERMOBALLISTIC ballistic sheets. Other examples ofsuitable stacks of unidirectional ballistic sheets 1005 for a ballisticpanel 100 can include a grouping of 2-20, 8-20, 12-20, 20-40, or 40-60unidirectional K-FLEX ballistic sheets. Still other examples of suitablestacks of unidirectional ballistic sheets 1005 for a ballistic panel 100can include a grouping of 2-20, 8-20, 12-20, 20-40, or 40-60 TENSYLONballistic sheets.

Panels Constructed from Double X-Ply Ballistic Sheets

Two x-ply ballistic sheets can be bonded together to produce aconfiguration known as double x-ply. Examples of suitable stacks ofdouble x-ply ballistic sheets 1005 for a flexible ballistic resistantpanel 100 can include a first plurality of double x-ply ballistic sheets1020 containing a first resin with a first melting temperature and asecond plurality of double x-ply ballistic sheets 1025 containing asecond resin with a second melting temperature (see, e.g., FIGS. 11 and12). The second melting temperature can be higher than the first meltingtemperature. Examples include: 1-10 0/90/0/90 double x-ply ballisticsheets containing a first resin and 1-10 0/90/0/90 double x-plyballistic sheets containing a second resin; 4-10 0/90/0/90 double x-plyballistic sheets containing a first resin and 4-10 0/90/0/90 doublex-ply ballistic sheets containing a second resin; 6-10 0/90 x-plyballistic sheets containing a first resin and 6-10 0/90/0/90 doublex-ply ballistic sheets containing a second resin; 10-15 0/90/0/90 doublex-ply ballistic sheets containing a first resin and 10-15 0/90/0/90double x-ply ballistic sheets containing a second resin; 15-20 0/90/0/90double x-ply ballistic sheets containing a first resin and 15-200/90/0/90 double x-ply ballistic sheets containing a second resin.

Examples of suitable stacks of double x-ply ballistic sheets 1005containing aramid fibers can include a first plurality of double x-plyballistic sheets containing aramid fibers and a first resin with a firstmelting temperature and a second plurality of double x-ply ballisticsheets containing aramid fibers and a second resin with a second meltingtemperature (see, e.g., FIGS. 11 and 12). The second melting temperaturecan be higher than the first melting temperature. Examples include: 1-100/90/0/90 double x-ply ballistic sheets containing a first resin and1-10 0/90/0/90 double x-ply ballistic sheets containing a second resin;4-10 0/90/0/90 double x-ply ballistic sheets containing a first resinand 4-10 0/90/0/90 double x-ply ballistic sheets containing a secondresin; 6-10 0/90/0/90 double x-ply ballistic sheets containing a firstresin and 6-10 0/90/0/90 double x-ply ballistic sheets containing asecond resin; 10-15 0/90/0/90 double x-ply ballistic sheets containing afirst resin and 10-15 0/90 x-ply ballistic sheets containing a secondresin; 15-20 0/90/0/90 double x-ply ballistic sheets containing a firstresin and 15-20 0/90/0/90 double x-ply ballistic sheets containing asecond resin.

Examples of suitable stacks of double x-ply ballistic sheets 1005 for aflexible ballistic resistant panel 100 can include a first plurality ofdouble x-ply ballistic sheets 1020 containing a polyethylene resin witha melting temperature of about 215-240 degrees F. and a second pluralityof double x-ply ballistic sheets 1025 containing a polypropylene resinwith a melting temperature of about 255-295 or 295-330 F (see, e.g.,FIGS. 11 and 12). Examples include: 1-10 0/90/0/90 double x-plyballistic sheets containing a polyethylene resin and 1-10 0/90/0/90double x-ply ballistic sheets containing a polypropylene resin; 4-100/90/0/90 double x-ply ballistic sheets containing a first resin and4-10 0/90/0/90 double x-ply ballistic sheets containing a polypropyleneresin; 6-10 0/90/0/90 double x-ply ballistic sheets containing apolyethylene resin and 6-10 0/90/0/90 double x-ply ballistic sheetscontaining a polypropylene resin; 10-15 0/90/0/90 double x-ply ballisticsheets containing a polyethylene resin and 10-15 0/90/0/90 double x-plyballistic sheets containing a polypropylene resin; 15-20 0/90/0/90double x-ply ballistic sheets containing a polyethylene resin and 15-200/90/0/90 double x-ply ballistic sheets containing a polypropyleneresin.

Examples of suitable stacks of double x-ply ballistic sheets 1005 for aballistic resistant panel 100 can include a first plurality ofTHERMOBALLISTIC ballistic sheets 1025 arranged in a stack having a topsurface and a bottom surface and bounded on the top surface by a firstplurality of K-FLEX ballistic sheets 1020 and bounded on the bottomsurface by a second plurality of K-FLEX ballistic sheets 1030, as shownin FIG. 11. Examples include: 1-5 K-FLEX 0/90/0/90 double x-plyballistic sheets, 1-5 THERMOBALLISTIC 0/90/0/90 double x-ply ballisticsheets, 1-5 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 2-5 K-FLEX0/90/0/90 double x-ply ballistic sheets, 2-5 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets, 2-5 K-FLEX 0/90/0/90 double x-plyballistic sheets; 3-5 K-FLEX 0/90/0/90 double x-ply ballistic sheets,3-5 THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets, 3-5 K-FLEX0/90/0/90 double x-ply ballistic sheets; 4 K-FLEX 0/90/0/90 double x-plyballistic sheets, 5 THERMOBALLISTIC 0/900/90 double x-ply ballisticsheets, 4 K-FLEX 0/900/90 double x-ply ballistic sheets; 3 K-FLEX0/90/0/90 double x-ply ballistic sheets, 4 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets, 3 K-FLEX 0/90/0/90 double x-ply ballisticsheets; 3 K-FLEX 0/90/0/90 double x-ply ballistic sheets, 4THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets, 3 K-FLEX0/90/0/90 double x-ply ballistic sheets; 2 K-FLEX 0/90/0/90 double x-plyballistic sheets, 4 THERMOBALLISTIC 0/90/0/90 double x-ply ballisticsheets, 2 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 5-15 K-FLEX0/90/0/90 double x-ply ballistic sheets, 5-15 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets, 5-15 K-FLEX 0/90/0/90 double x-plyballistic sheets; or 15-20 K-FLEX 0/90/0/90 double x-ply ballisticsheets, 15-20 THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets,15-20 K-FLEX 0/90/0/90 double x-ply ballistic sheets.

Examples of suitable stacks of double x-ply ballistic sheets 1005 for aflexible ballistic resistant panel 100 can include a first plurality ofK-FLEX ballistic sheets 1025 arranged in a stack having a top surfaceand a bottom surface and bounded on the top surface by a first pluralityof THERMOBALLISTIC ballistic sheets 1020 and bounded on the bottomsurface by a second plurality of THERMOBALLISTIC ballistic sheets 1030,as shown in FIG. 12. Examples include: 1-5 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets, 1-5 K-FLEX 0/90/0/90 double x-plyballistic sheets, 1-5 THERMOBALLISTIC 0/90/0/90 double x-ply ballisticsheets; 2-5 THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets, 2-5K-FLEX 0/90/0/90 double x-ply ballistic sheets, 2-5 THERMOBALLISTIC0/90/0/90 double x-ply ballistic sheets; 3-5 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets, 3-5 K-FLEX 0/90/0/90 double x-plyballistic sheets, 3-5 THERMOBALLISTIC 0/90/0/90 double x-ply ballisticsheets; 4 THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets, 5K-FLEX 0/900/90 double x-ply ballistic sheets, 4 THERMOBALLISTIC0/900/90 double x-ply ballistic sheets; 3 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets, 4 K-FLEX 0/90/0/90 double x-ply ballisticsheets, 3 THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets; 3THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets, 4 K-FLEX0/90/0/90 double x-ply ballistic sheets, 3 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets; 2 THERMOBALLISTIC 0/90/0/90 double x-plyballistic sheets, 4 K-FLEX 0/90/0/90 double x-ply ballistic sheets, 2THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets; 5-15THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets, 5-15 K-FLEX0/90/0/90 double x-ply ballistic sheets, 5-15 THERMOBALLISTIC 0/90/0/90double x-ply ballistic sheets; or 15-20 THERMOBALLISTIC 0/90/0/90 doublex-ply ballistic sheets, 15-20 K-FLEX 0/90/0/90 double x-ply ballisticsheets, 15-20 THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets.

Examples of suitable stacks of double x-ply ballistic sheets 1005 for aflexible ballistic resistant panel 100 can include a grouping of 1-10,4-10, 6-10, 10-15, or 15-20 double x-ply ballistic sheets made of fiberssuch as, for example, aramid or UHMWPE fibers. Examples of suitablestacks of double x-ply ballistic sheets 1005 for a ballistic panel 100can include a grouping of 1-10, 4-10, 6-10, 10-15, or 15-20THERMOBALLISTIC 0/90/0/90 double x-ply ballistic sheets. Other examplesof suitable stacks of double x-ply ballistic sheets 1005 for a ballisticpanel 100 can include a grouping of 1-10, 4-10, 6-10, 10-15, or 15-20K-FLEX 0/90/0/90 double x-ply ballistic sheets.

Panels Constructed from Uni-Ply, X-Ply, or Double X-Ply Ballistic Sheets

Although specific examples of stacks made exclusively of uni-ply, x-ply,or double x-ply ballistic sheets are provided herein, these examples arenot limiting. Suitable stacks can include any combination of uni-ply,x-ply, double-x ply, triple x-ply, or other more elaborate multilayeredballistic sheets. In any of the examples provided herein, two uni-plyballistic sheets can be substituted for an x-ply ballistic sheet, anx-ply ballistic sheet can be substituted for two uni-ply ballisticsheets, four uni-ply ballistic sheets can be substituted for a doublex-ply ballistic sheet, a double x-ply ballistic sheet can be substitutedfor four uni-ply ballistic sheets, two x-ply ballistic sheets can besubstituted for a double x-ply ballistic sheets, and a double x-plyballistic sheet can be substituted for two x-ply ballistic sheets.

Panels Constructed from Ballistic Sheets and Fiberglass Sheets

One or more fiberglass sheets (e.g. sheets made of woven glass fibers orsheets made of glass fibers arranged unidirectionally into uni-ply orx-ply), can be incorporated into any of the various stacks of ballisticsheets described herein to form a ballistic resistant panel (see, e.g.FIG. 13). Fiberglass sheets have several attributes that make themdesirable for inclusion in a ballistic resistant panel. Specifically,fiberglass sheets are less expensive than sheets made of aramid fibers,which translates to lower cost panels. Also, fiberglass sheets canenhance stab resistance of the panel 100. The fiberglass sheets can haveany suitable thickness depending on the application of the panel. Forexample, for applications that require flexible panels, the thickness ofeach fiberglass sheet can be about 0.006, 0.009, 0.010, 0.005-0.020,0.010-0.020, or 0.020-0.030 inches.

Examples of suitable stacks of ballistic sheets for a ballisticresistant panel can include a plurality of x-ply ballistic sheetscontaining aramid fibers and a first resin with a first meltingtemperature and a plurality of fiberglass sheets containing glass fibers(see, e.g. FIG. 13). Examples include: 1-10 x-ply ballistic sheetscontaining aramid fibers and resin and 1-10 fiberglass sheets; 4-10x-ply ballistic sheets containing aramid fibers and resin and 4-10fiberglass sheets; 6-10 x-ply ballistic sheets containing aramid fibersand resin and 6-10 fiberglass sheets; 10-15 x-ply ballistic sheetscontaining aramid fibers and resin and 10-15 fiberglass sheets; 15-20x-ply ballistic sheets containing aramid fibers and resin and 15-20fiberglass sheets.

Examples of suitable stacks of ballistic sheets for a ballisticresistant panel 100 can include a first plurality of x-ply ballisticsheets containing a polyethylene resin with a melting temperature ofabout 215-240 degrees F. and a plurality of s-glass sheets (see, e.g.FIG. 13). Suitable examples include: 1-10 0/90 x-ply ballistic sheetscontaining a polyethylene resin and 1-10 s-glass fiberglass sheets; 4-100/90 x-ply ballistic sheets containing a polyethylene resin and 4-10s-glass fiberglass sheets; 6-10 0/90 x-ply ballistic sheets containing apolyethylene resin and 6-10 s-glass fiberglass sheets; 10-20 0/90 x-plyballistic sheets containing a polyethylene resin and 10-20 s-glassfiberglass sheets; 20-30 0/90 x-ply ballistic sheets containing apolyethylene resin and 20-30 s-glass fiberglass sheets.

Examples of suitable stacks of ballistic sheets 1005 for a ballisticresistant panel 100 can include a first plurality of s-glass fiberglasssheets 1025 arranged in a stack having a top surface and a bottomsurface and bounded on the top surface by a first plurality of K-FLEXballistic sheets 1020 and bounded on the bottom surface by a secondplurality of K-FLEX ballistic sheets 1030, as shown in FIG. 13. Examplesinclude: 1-10 K-FLEX 0/90 x-ply ballistic sheets, 1-10 s-glassfiberglass sheets, 1-10 K-FLEX 0/90 x-ply ballistic sheets; 4-10 K-FLEX0/90 x-ply ballistic sheets, 4-10 s-glass fiberglass sheets, 4-10 K-FLEX0/90 x-ply ballistic sheets; 6-10 K-FLEX 0/90 x-ply ballistic sheets,6-10 s-glass fiberglass sheets, 6-10 K-FLEX 0/90 x-ply ballistic sheets;8 K-FLEX 0/90 x-ply ballistic sheets, 10 s-glass fiberglass sheets, 8K-FLEX 0/90 x-ply ballistic sheets; 8 K-FLEX 0/90 x-ply ballisticsheets, 5-7 s-glass fiberglass sheets, 8 K-FLEX 0/90 x-ply ballisticsheets; 6 K-FLEX 0/90 x-ply ballistic sheets, 8 s-glass fiberglasssheets, 6 K-FLEX 0/90 x-ply ballistic sheets; 5 K-FLEX 0/90 x-plyballistic sheets, 8 s-glass fiberglass sheets, 5 K-FLEX 0/90 x-plyballistic sheets; 4 K-FLEX 0/90 x-ply ballistic sheets, 8 s-glassfiberglass sheets, 4 K-FLEX 0/90 x-ply ballistic sheets; 6 K-FLEX 0/90x-ply ballistic sheets, 6 s-glass fiberglass sheets, 6 K-FLEX 0/90 x-plyballistic sheets; 5 K-FLEX 0/90 x-ply ballistic sheets, 5 s-glassfiberglass sheets, 5 K-FLEX 0/90 x-ply ballistic sheets; or 2 or moreK-FLEX 0/90 x-ply ballistic sheets, 1 or more s-glass fiberglass sheets,2 or more K-FLEX 0/90 x-ply ballistic sheets.

Suitable stacks can include one or more uni-ply ballistic sheets and oneor more fiberglass sheets. Examples include: 1-20 K-FLEX uni-plyballistic sheets, 1-10 s-glass fiberglass sheets, 1-20 K-FLEX uni-plyballistic sheets; 8-20 K-FLEX uni-ply ballistic sheets, 4-10 s-glassfiberglass sheets, 8-20 K-FLEX uni-ply ballistic sheets; 12-20 K-FLEXuni-ply ballistic sheets, 6-10 s-glass fiberglass sheets, 12-20 K-FLEXuni-ply ballistic sheets; 16 K-FLEX uni-ply ballistic sheets, 10 s-glassfiberglass sheets, 16 K-FLEX uni-ply ballistic sheets; 16 K-FLEX uni-plyballistic sheets, 5-7 s-glass fiberglass sheets, 16 K-FLEX uni-plyballistic sheets; 12 K-FLEX uni-ply ballistic sheets, 8 s-glassfiberglass sheets, 12 K-FLEX uni-ply ballistic sheets; 10 K-FLEX uni-plyballistic sheets, 8 s-glass fiberglass sheets, 10 K-FLEX uni-plyballistic sheets; 8 K-FLEX uni-ply ballistic sheets, 8 s-glassfiberglass sheets, 8 K-FLEX uni-ply ballistic sheets; 12 K-FLEX uni-plyballistic sheets, 6 s-glass fiberglass sheets, 12 K-FLEX 0/90 x-plyballistic sheets; or 10 K-FLEX uni-ply ballistic sheets, 5 s-glassfiberglass sheets, 10 K-FLEX uni-ply ballistic sheets; or 2 or moreK-FLEX uni-ply ballistic sheets, 1 or more s-glass fiberglass sheets, 2or more K-FLEX uni-ply ballistic sheets.

Suitable stacks can include one or more double x-ply ballistic sheetsand one or more fiberglass sheets. Examples include: 1-10 K-FLEX0/90/0/90 double x-ply ballistic sheets, 1-10 s-glass fiberglass sheets,1-10 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 2-5 K-FLEX0/90/0/90 double x-ply ballistic sheets, 4-10 s-glass fiberglass sheets,2-5 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 6-10 K-FLEX0/90/0/90 double x-ply ballistic sheets, 6-10 s-glass fiberglass sheets,3-5 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 4 K-FLEX 0/90/0/90double x-ply ballistic sheets, 10 s-glass fiberglass sheets, 4 K-FLEX0/90/0/90 double x-ply ballistic sheets; 4 K-FLEX 0/90/0/90 double x-plyballistic sheets, 5-7 s-glass fiberglass sheets, 4 K-FLEX 0/90/0/90double x-ply ballistic sheets; 3 K-FLEX 0/90/0/90 double x-ply ballisticsheets, 4-8 s-glass fiberglass sheets, 3 K-FLEX 0/90/0/90 double x-plyballistic sheets; 2 K-FLEX 0/90/0/90 double x-ply ballistic sheets, 4-8s-glass fiberglass sheets, 2 K-FLEX 0/90/0/90 double x-ply ballisticsheets; 4 K-FLEX 0/90/0/90 double x-ply ballistic sheets, 8 s-glassfiberglass sheets, 4 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 3K-FLEX 0/90/0/90 double x-ply ballistic sheets, 6 s-glass fiberglasssheets, 3 K-FLEX 0/90/0/90 double x-ply ballistic sheets; 3 K-FLEX0/90/0/90 double x-ply ballistic sheets, 5 s-glass fiberglass sheets, 3K-FLEX 0/90/0/90 double x-ply ballistic sheets; or 2 or more K-FLEX0/90/0/90 double x-ply ballistic sheets, 1 or more s-glass fiberglasssheets, 2 or more K-FLEX 0/90/0/90 double x-ply ballistic sheets.

Methods or Manufacturing Flexible Ballistic Resistant Panels

A method of manufacturing a ballistic resistant panel 100 can includeproviding a stack of ballistic sheets 1005, inserting the stack ofballistic sheets into a vacuum bag 1310, evacuating air from the vacuumbag, and heating the stack of ballistic sheets in the vacuum bag to apredetermined temperature for a predetermined duration. In someexamples, the predetermined temperature can be about 250-550, 225-550,225-350, 250-300, 250-275, 265-275, 225-250, or 200-240 degrees F., andthe predetermined duration can be about 1, 5, 15-30, 30-60, 45-60,60-120, 120-240, or 240-480 minutes. The method can include applying apredetermined pressure to the stack of ballistic sheets in the vacuumbag for a second predetermined duration. The predetermined pressure canbe about 10-100, 50-75, 75-100, 100-500, 500-1,000, 1,000-2,500,2,500-15,000, or 15,000-30,000 psi, and the second predeterminedduration can be about 1, 5, 15-30, 30-60, 45-60, 60-120, 120-240, or240-480 minutes. The step of heating the stack of ballistic sheets inthe vacuum bag to the predetermined temperature for the predeterminedduration can occur concurrently with applying the predetermined pressureto the stack of ballistic sheets in the vacuum bag 1310 for the secondpredetermined duration. The method can include encasing the stack ofballistic sheets 1005 in a waterproof cover 1105 prior to inserting thestack of ballistic sheets into the vacuum bag 1310. The waterproof cover1105 can be made of nylon coated with polyurethane, polypropylene,polyethylene, or polyvinylchloride.

With respect to the method described above, the stack of ballisticsheets 1005 can include a first plurality of ballistic sheets 1020having a first resin with a melting temperature of about 215-240,240-265, 265-295, or 295-340 degrees F. The stack 1005 can also includea second plurality of ballistic sheets 1025 adjacent to the firstplurality of ballistic sheets, where the second plurality of ballisticsheets have a second resin with a melting temperature of about 255-295,295-330, 330-355, or 355-375 degrees F. The stack 1005 can also includea third plurality of ballistic sheets 1030 adjacent to the secondplurality of ballistic sheets, where the third plurality of ballisticsheets have a third resin with a melting temperature of about 215-240,240-265, 265-295, or 295-340 degrees F. The first plurality of ballisticsheets 1020 can include 1-10, 10-20, or 20-30 x-ply ballistic sheets,where the ballistic sheets are made of aramid fibers and the first resinis made of polyethylene. The second plurality of ballistic sheets 1025can include 1-10, 10-20, or 20-30 x-ply ballistic sheets, where theballistic sheets are made of aramid fibers and the second resin is madeof polypropylene. Similar to the first plurality of ballistic sheets1020, the third plurality of ballistic sheets 1030 can include 1-10,10-20, or 20-30 x-ply ballistic sheets, where the ballistic sheets aremade of aramid fibers and the third resin is made of polyethylene.

Following the heating and pressure steps described above, the method canalso include a step of cooling the stack of ballistic sheets 1005 in thevacuum bag 1310 from the predetermined temperature to room temperature.Cooling can occur using any suitable heat transfer method, such asnatural convection, forced convection, or conduction (e.g. by submergingthe waterproof panels 100 in a cooling bath).

In some methods of manufacturing flexible ballistic resistant panels100, a stack of ballistic sheets 1005 can be provided where the stackhas a first plurality of ballistic sheets 1020, a second plurality ofballistic sheets 1025 adjacent to the first plurality of ballisticsheets, and a third plurality of ballistic sheets 1030 adjacent to thesecond plurality of ballistic sheets. Each of the first plurality ofballistic sheets 1020 can be formed of a first arrangement of aramidfibers, where the first arrangement of aramid fibers defines atwo-dimensional pattern. The first plurality of ballistic sheets 1020can be stacked according to the two-dimensional pattern. Each of thesecond plurality of ballistic sheets 1025 can be formed of a secondarrangement of aramid fibers, where the second arrangement of aramidfibers substantially conforms to the two-dimensional pattern. The secondplurality of ballistic sheets 1025 can be stacked according to thetwo-dimensional pattern. Each of the third plurality of ballistic sheets1030 can be formed of a third arrangement of aramid fibers, where thethird arrangement of aramid fibers substantially conforms to thetwo-dimensional pattern. The third plurality of ballistic sheets 1030can be stacked according to the two-dimensional pattern. The firstplurality of ballistic sheets 1020, the second plurality of ballisticsheets 1025, and the third plurality of ballistic sheets 1030 can beformed in a stack 1005 according to the two-dimensional pattern. Themethod can include inserting the stack of ballistic sheets 1005 into avacuum bag 1310 and evacuating air from the vacuum bag. The method caninclude heating the stack of ballistic sheets 1005 to a predeterminedtemperature for a predetermined duration. The predetermined temperaturecan be between about 200 and 500 degrees F. and, more specifically,about 250-300, 265-275, 225-250, or 200-240 degrees F. The predeterminedduration can be at least 5 minutes and, more specifically, about 30-45,45-60, or 60-120 minutes. The method can include applying apredetermined pressure to the stack of ballistic sheets 1005 in thevacuum bag 1310 for a second predetermined duration. The predeterminedpressure can be at least 10 psi, and the second predetermined durationis at least 5 minutes. More specifically, the predetermined pressure canbe about 10-100, 50-75, or 75-100 psi, and the second predeterminedduration can be about 30-45, 45-60, 60-120, 120-240, 240-480 minutes.

In the method described above, applying the predetermined pressure tothe stack of ballistic sheets 1005 in the vacuum bag 1310 for the secondpredetermined duration can occur concurrently with heating the stack ofballistic sheets in the vacuum bag to the predetermined temperature forthe predetermined duration. The method can include encasing the stack ofballistic sheets 1005 in a waterproof cover 1105, as shown in FIG. 7,prior to inserting the stack of ballistic sheets into the vacuum bag1310. The waterproof cover can be made of nylon coated withpolyurethane, polyvinylchloride, polypropylene, or polyethylene.

In the method described above, the first plurality of ballistic sheets1020 can include a first resin with a melting temperature of about215-240 degrees F., the second plurality of ballistic sheets 1025 caninclude a second resin with a melting temperature of about 255-295degrees F., and the third plurality of ballistic sheets 1030 can includea third resin with a melting temperature of about 215-240 degrees F. Topromote partial or full bonding of the ballistic sheets within the firstand third pluralities of ballistic sheets (and to avoid bonding of theballistic sheets within second plurality of ballistic sheets 1025), thepredetermined temperature can be about 200-240 or 225-250 degrees F.,which is below the melting temperature of the second resin.

In another example, the first plurality of ballistic sheets 1020 caninclude a first resin with a melting temperature of about 215-240degrees F., the second plurality of ballistic sheets 1025 can include asecond resin with a melting temperature of about 295-330 degrees F., andthe third plurality of ballistic sheets 1030 can include a third resinwith a melting temperature of about 215-240 degrees F. To promotepartial or full bonding of the ballistic sheets within the first andthird pluralities of ballistic sheets (and to avoid bonding of theballistic sheets within second plurality of ballistic sheets 1025), thepredetermined temperature can be about 200-240, 225-250, or 265-275degrees F., which is below the melting temperature of the second resin.In this example, the first plurality of ballistic sheets 1020 caninclude 1-10 K-FLEX 0/90 x-ply ballistic sheets, the second plurality ofballistic sheets 1025 can include 1-10 THERMOBALLISTIC 0/90 x-plyballistic sheets, and the third plurality of ballistic sheets 1030 caninclude 1-10 K-FLEX 0/90 x-ply ballistic sheets.

The method described above can further include cooling the stack ofballistic sheets 1005 in the vacuum bag from the predeterminedtemperature to room temperature. The method can also include subjectingthe panel 100 to a break-in process to enhance its flexibility.

Flexible Ballistic Panel Having a Plurality of Ballistic Sheets

In one example, as shown in FIG. 10, a flexible ballistic resistantpanel can include a plurality of ballistic sheets (i.e. a stack ofballistic sheets 1005). Each of the plurality of ballistic sheets 1005can be formed of an arrangement of higher performance fibers (e.g.aramid fibers), and the arrangement of high performance fibers candefine a two-dimensional pattern. The plurality of ballistic sheets canbe stacked according to the two-dimensional pattern, where each of theplurality of ballistic sheets is at least partially bonded to at leastone adjacent ballistic sheet in the plurality of ballistic sheets. Insome examples, the plurality of ballistic sheets 1005 can include 1-10,10-20, or 20-30 ballistic sheets. The plurality of ballistic sheets 1005can be made of a plurality of high performance fibers coated with athermoplastic polymer resin. The thermoplastic polymer resin can have amelting temperature of about 215-240, 240-265, 265-295, 295-340,340-355, or 355-375 degrees F.

In another example, as shown in FIG. 10, a flexible ballistic resistantpanel 100 can include a plurality of ballistic sheets 1005. Each of theplurality of ballistic sheets can be formed of an arrangement of highperformance fibers, such as thermoplastic polyethylene fibers (e.g.UHMWPE fibers), and the arrangement of thermoplastic polyethylene fiberscan define a two-dimensional pattern. The plurality of ballistic sheets1005 can be stacked according to the two-dimensional pattern, where eachof the plurality of ballistic sheets is at least partially bonded to atleast one adjacent ballistic sheet in the plurality of ballistic sheets.In some examples, the plurality of ballistic sheets can include 1-10,10-20, or 20-30 ballistic sheets made of thermoplastic polyethylenefabric, such as TENSYLON.

The plurality of ballistic sheets 1005, whether containing aramidfibers, thermoplastic polyethylene fibers, or both, can be encased by awaterproof cover 1105, as shown in FIG. 10. The waterproof cover 1105can be made of any suitable material, such as rubber, NYLON, RAYON,ripstop NYLON, CORDURA, polyvinyl chloride, polyurethane, siliconeelastomer, or fluoropolymer. The waterproof cover 1105 can be adhered toan outer surface of the plurality of ballistic sheets 1005 to preventmovement of the plurality of ballistic sheets relative to the waterproofcover. The flexible ballistic resistant panel 100 can include a coatingon the inner surface of the waterproof cover. The coating can improvewater resistance and can serve as an adhesive layer. The coating can bemade of polyurethane, polyvinylchloride, polyethylene, or polypropylene.

Flexible Ballistic Panel Having First and Second Pluralities ofBallistic Sheets

A flexible ballistic resistant panel 100 can include a first pluralityof ballistic sheets 1020 made of aramid fibers and coated with a firstresin having a first melting temperature. The flexible ballisticresistant panel can also include a second plurality of ballistic sheets1025 adjacent to the first plurality of ballistic sheets, where thesecond plurality of ballistic sheets are made of aramid fibers coatedwith a second resin having a second melting temperature. The secondmelting temperature can be greater than the first melting temperature.The first resin can be a thermoplastic polymer with a meltingtemperature of about 215-240 degrees F. The second resin can be athermoplastic polymer with a melting temperature of about 255-295 or295-330 degrees F. In some examples, the first resin can bepolyethylene, and the second resin can be polypropylene. The firstplurality of ballistic sheets 1020 can include about 1-10, 10-20, or20-30 ballistic sheets. Similarly, the second plurality of ballisticsheets 1025 can include about 1-10, 10-20, or 20-30 ballistic sheets. Incertain examples, the first plurality of ballistic sheets 1020 caninclude 1-10, 10-20, or 20-30 K-FLEX 0/90 x-ply ballistic sheets, andthe second plurality of ballistic sheets 1025 can include 1-10, 10-20,or 20-30 THERMOBALLISTIC 0/90 x-ply ballistic sheets. In some examples,the first plurality of ballistic sheets 1020 can include 5-10 K-FLEX0/90 x-ply ballistic sheets, and the second plurality of ballisticsheets 1025 can include 5-10 THERMOBALLISTIC 0/90 x-ply ballisticsheets. The flexible ballistic resistant panel 100 can include awaterproof cover 1105 encasing the first and second pluralities ofballistic sheets (1020, 1025). The waterproof cover 1105 can be made ofany suitable material, such as nylon coated with polyurethane,polypropylene, polyvinylchloride, or polyethylene.

Flexible Ballistic Panel Having First, Second, and Third Pluralities ofBallistic Sheets

A flexible ballistic resistant panel 100 can include a first pluralityof ballistic sheets 1020, each of the first plurality of ballisticsheets 1020 being formed of a first arrangement of aramid fibers. Thefirst arrangement of aramid fibers can define a two-dimensional pattern,and the first plurality of ballistic sheets 1020 can be stackedaccording to the two-dimensional pattern. The flexible ballisticresistant panel 100 can include a second plurality of ballistic sheets1025 adjacent to the first plurality of ballistic sheets. Each of thesecond plurality of ballistic sheets 1025 can be formed of a secondarrangement of aramid fibers. The second arrangement of aramid fiberscan substantially conform to the two-dimensional pattern, and the secondplurality of ballistic sheets can be stacked according to thetwo-dimensional pattern. The flexible ballistic resistant panel 100 caninclude a third plurality of ballistic sheets 1030 adjacent to thesecond plurality of ballistic sheets. Each of the third plurality ofballistic sheets 1030 can be formed of a third arrangement of aramidfibers. The third arrangement of aramid fibers can substantially conformto the two-dimensional pattern, and the third plurality of ballisticsheets 1030 can be stacked according to the two-dimensional pattern. Thefirst plurality of ballistic sheets 1020, the second plurality ofballistic sheets 1025, and the third plurality of ballistic sheets 1030can be formed in a stack 1005 according to the two-dimensional pattern.The flexible ballistic resistant panel 100 can include a waterproofcover 1105 encasing the first plurality of ballistic sheets 1020, thesecond plurality of ballistic sheets 1025, and the third plurality ofballistic sheets 1030. Within the panel 100, each of the first pluralityof ballistic sheets 1020 can be at least partially bonded to at leastone adjacent ballistic sheet in the first plurality of ballistic sheets.Likewise, each of the third plurality of ballistic sheets 1030 can be atleast partially bonded to at least one adjacent ballistic sheet in thethird plurality of ballistic sheets.

The first plurality of ballistic sheets 1020 can include 1-10, 10-20, or20-30 ballistic sheets, the second plurality of ballistic sheets 1025can include 1-10, 10-20, or 20-30 ballistic sheets, and the thirdplurality of ballistic sheets 1030 can include 1-10, 10-20, or 20-30ballistic sheets. In some examples, where the flexible ballisticresistant panel 100 is configured to be certified as Type IIIA flexiblearmor under NIJ Standard-0101.06, the first plurality of ballisticsheets 1020 can include 5-10 or 6-8 ballistic sheets, the secondplurality of ballistic sheets 1025 can include 5-10 or 6-8 ballisticsheets, and the third plurality of ballistic sheets 1030 can include5-10 or 6-8 ballistic sheets. In some examples, the first plurality ofballistic sheets 1020 can be K-FLEX 0/90 x-ply ballistic sheets, thesecond plurality of ballistic sheets 1025 can be THERMOBALLISTIC 0/90x-ply ballistic sheets, and the third plurality of ballistic sheets 1030can be K-FLEX 0/90 x-ply ballistic sheets. The panel 100 can have athickness of less than 0.5, 0.375, or 0.25 inches, and where the panelis configured to be certified as Type IIIA flexible armor under NIJStandard-0101.06, can have a thickness of 0.15-0.22 or about 0.215inches.

The first plurality of ballistic sheets 1020 can include a first resinmade of polyethylene and having a melting temperature of about 215-240,240-265, 265-295, or 295-340 degrees F. The second plurality ofballistic sheets 1025 can include a second resin made of polypropyleneand having a melting temperature of about 255-295, 295-330, 330-355, or355-375 degrees F. The third plurality of ballistic sheets 1030 caninclude a third resin made of polyethylene and having a meltingtemperature of about 215-240, 240-265, 265-295, or 295-340 degrees F.

In some examples, the flexible ballistic resistant panel 100 can includea first plurality of ballistic sheets 1020 made of high performancefibers, such as aramid fibers. Each ballistic sheet within the firstplurality of ballistic sheets 1020 can be at least partially bonded toat least one adjacent ballistic sheet in the first plurality ofballistic sheets. The panel 100 can include a second plurality ofballistic sheets 1025 made of high performance fibers, such as aramidfibers. The second plurality of ballistic sheets 1025 can be positionedadjacent to the first plurality of ballistic sheets 1020. The panel 100can include a third plurality of ballistic sheets 1030 made of highperformance fibers, such as aramid fibers. The third plurality ofballistic sheets 1030 can be positioned adjacent to the second pluralityof ballistic sheets 1025. Each ballistic sheet within the thirdplurality of ballistic sheets 1030 can be at least partially bonded toat least one adjacent ballistic sheet in the third plurality ofballistic sheets. The first plurality of ballistic sheets 1020 caninclude 1-10, 10-20, or 20-30 ballistic sheets, the second plurality ofballistic sheets 1025 can include 1-10, 10-20, or 20-30 ballisticsheets, and the third plurality of ballistic sheets 1030 can include1-10, 10-20, or 20-30 ballistic sheets. In certain examples, firstplurality of ballistic sheets 1020 can include 1-10 K-FLEX 0/90 x-plyballistic sheets, the second plurality of ballistic sheets 1025 caninclude 1-10 THERMOBALLISTIC 0/90 x-ply ballistic sheets or s-glassfiberglass sheets, and the third plurality of ballistic sheets 1030 caninclude 1-10 K-FLEX 0/90 x-ply ballistic sheets. The panel 100 caninclude a waterproof cover encasing a stack of ballistic sheets 1005consisting of the first plurality of ballistic sheets 1020, the secondplurality of ballistic sheets 1025, and the third plurality of ballisticsheets 1030. In some examples, the waterproof cover 1105 can be made ofnylon coated with polyurethane, polypropylene, polyethylene, orpolyvinylchloride. A first resin in the first plurality of ballisticsheets 1020 can have a melting temperature of about 215-240, 240-265,265-295, or 295-340 degrees F. A second resin in the second plurality ofballistic sheets 1025 can have a melting temperature of about 255-295,295-330, 330-355, or 355-375 degrees F. A third resin in the thirdplurality of ballistic sheets can have a melting temperature of about215-240, 240-265, 265-295, or 295-340 degrees F.

Stitching

The flexible ballistic resistant panels 100 described herein do notrequire stitching to be as effective, or more effective, than existingpanels with similar dimensions. However, where added labor costs are nota primary concern, the panels described herein can include stitches,such as quilt stitches, radial stitches, row stitches, box stitches, ora combination thereof. Stitches can be added to the stack of ballisticsheets at any stage in the manufacturing process, including beforevacuum bagging, after vacuum bagging, before heating, after heating,before applying pressure, after applying pressure, etc. Stitches may bedesirable to defend against certain types of ballistic threats.

Reversible Panel

Many ballistic resistant panels are designed to have a strike face (see,e.g. the ceramic plate 32 in FIG. 5) and a wear face. A strike face is asurface that is designed to face an incoming ballistic threat, and awear face is a surface that is designed to face the wearer's torso.Panels with a strike face are directional and must be oriented with thestrike face facing toward an incoming projectile. If the panel isimproperly oriented and a projectile strikes the wear face, the panelwill likely fail to perform at the panel's certification level. Forexample, if a soldier inserts a ballistic resistant panel into a carriervest, but accidentally orients the panel with the wear face directedoutward, the panel may fail to perform according to its certificationlevel when struck by a projectile, and the projectile may pass throughthe panel.

To ensure consistent performance of the ballistic resistant panelregardless of its orientation, it can be desirable to create a panel 100that does not have a wear face. Instead, the panel 100 can besymmetrical or nearly symmetrical from a front surface to a back surface(e.g. the panel can have a symmetrical arrangement of ballistic sheets),thereby permitting either side of the panel to serve as a strike facewithout altering performance. In other instances, it may be suitable tohave a non-symmetrical panel. For example, a non-symmetrical panel maybe suitable where the panel will be permanently or semi-permanentlyinstalled (e.g. in a vehicle door or around an oil or gas pipeline),since the panel will not be moved often and, therefore, the risk of userinstallation error is greatly diminished or eliminated entirely.

Multiple Stacks of Ballistic Sheets

Two or more stacks of ballistic sheets 1005 can be combined to provideadditional protection against ballistic threats. For example, two ormore stacks of ballistic sheets 1005 can be combined to form a stack ofpanels 200, as shown in FIGS. 14-16. In one example shown in FIG. 15,two stacks of ballistic sheets 1005 can be combined within a singlewaterproof cover 1105 to form a combined stack of ballistic sheets 4005.The combined stack 4005 can include a first plurality of ballisticsheets 1020, a second plurality of ballistic sheets 1025, a thirdplurality of ballistic sheets 1030, a fourth plurality of ballisticsheets 1035, and a fifth plurality of ballistic sheets 1040. Thisconfiguration can be desirable in situations where ballistic performanceis more important than flexibility, since flexibility will decrease asthe number of ballistic sheets in the stack increases. In this example,the third plurality 1030 may in fact be two pluralities of the same typeof ballistic sheets that are shown as a single plurality of ballisticsheets after the two separate stacks are arranged into a combined stack.

In some examples, the stack of panels 200 can include two or moreflexible panels 100. FIG. 14 shows a stack of panels 200 containing twoflexible ballistic resistant panels 100. FIG. 16 shows a stack of panels200 containing three flexible ballistic resistant panels 100. Eachflexible panel 100 can include its own waterproof cover 1105, and thestack of panels 200 can include an additional waterproof cover 4105 toprovide even greater protection against water intrusion. For example, ifthe additional waterproof cover 4105 is torn during use, the individualwaterproof covers 1105 will protect each stack of ballistic sheets 1005within each flexible panel 100 from water intrusion.

Modular Armor Systems

A modular armor system can include a carrier vest 30, similar to thevest shown in FIG. 5, configured to receive one or more flexibleballistic resistant panels 100 as described herein. The carrier vest maybe adapted to fit a human torso and may include a pouch adapted toreceive and store the one or more flexible ballistic resistant panels100. Each flexible ballistic resistant panel 100 can include a portionof hook and loop fastener (or other suitable fastener) attached to anexterior surface of the panel. The fastener can permit a user to quicklyadd or remove panels 100 as needed to protect against ballistic threats.In one example, a soldier can modify the number of panels 100 in a stackof panels disposed in the pouch of the carrier vest 30 based on a threatlevel of a combat situation. If the threat level is higher thanexpected, the soldier can add one or more additional panels 100 to thestack for added protection. Alternately, if the threat level is lowerthan expected, the soldier can remove one or more panels from the stackof panels to reduce the weight of the stack, increase the flexibility ofthe stack, and thereby enhance the soldier's mobility.

In some examples, a modular armor system can include a carrier vest 30adapted to fit a human torso, where the carrier vest includes a pouchadapted to receive and store one or more flexible ballistic resistantpanels 100 as described herein. The one or more flexible ballisticresistant panels 100 can be adapted to fit inside the pouch of thecarrier vest. Each of the flexible ballistic resistant panels 100 caninclude at least a first plurality of ballistic sheets 1020 and a secondplurality of ballistic sheets 1025. The first plurality of ballisticsheets 1020 can be made of aramid fibers and a can be coated with afirst resin having a first melting temperature. Similarly, the secondplurality of ballistic sheets 1025, which can be adjacent to the firstplurality of ballistic sheets 1020, can be made of aramid fibers and canbe coated with a second resin having a second melting temperature, wherethe second melting temperature is greater than the first meltingtemperature.

Each of the one or more flexible ballistic resistant panels 100 caninclude a portion of hook and loop fastener attached to an exteriorsurface of the panel. The portion of hook and loop fastener can allowthe flexible ballistic resistant panel 100 to be removably attached to asecond flexible ballistic resistant panel 100 to prevent relativeshifting. The first resin can be a thermoplastic polymer having amelting temperature of about 215-240 degrees F. The second resin can bea thermoplastic polymer having a melting temperature of about 255-295 or295-330 degrees F. In some examples, the first resin can bepolyethylene, and the second resin can be polypropylene. Within eachflexible ballistic resistant panel 100, the first plurality of ballisticsheets 1020 can include 1-10, 10-20, or 20-30 ballistic sheets, such asK-FLEX 0/90 x-ply ballistic sheets, and the second plurality ofballistic sheets 1025 can include 1-10, 10-20, or 20-30 ballisticsheets, such as THERMOBALLISTIC 0/90 x-ply ballistic sheets.

Protective Cover for Oil or Gas Pipeline

A flexible ballistic resistant panel 100 can be adapted to serve as aballistic resistant cover for an oil or gas pipeline. The flexibleballistic resistant panel 100 can include a plurality of ballisticsheets 1005, and each of the plurality of ballistic sheets can be formedof an arrangement of high performance fibers. The arrangement of highperformance fibers can define a two-dimensional pattern. The pluralityof ballistic sheets 1005 can be stacked according to the two-dimensionalpattern. Within the stack 1005, each of the plurality of ballisticsheets can be at least partially bonded to at least one adjacentballistic sheet in the plurality of ballistic sheets. The flexibleballistic resistant panel 100 can also include a waterproof cover 1105encasing the plurality of ballistic sheets. In some examples, thewaterproof cover 1105 can include an adhesive coating on an innersurface. The adhesive coating can adhere the waterproof cover 1105 to anouter surface of the plurality of ballistic sheets to prevent movementof the waterproof cover relative to the plurality of ballistic sheets.The adhesive coating can be made of polyurethane, polyvinylchloride,polyethylene, or polypropylene. The waterproof cover 1105 can be made ofrubber, NYLON, RAYON, ripstop NYLON, CORDURA, polyvinyl chloride,polyurethane, silicone elastomer, or fluoropolymer. The waterproof cover1105 can be coated with an ultraviolet (UV) protectant to limit damagefrom sunlight exposure.

In some examples, the flexible ballistic resistant panel 100 can includea magnetic attachment feature configured to allow quick and easymounting of the flexible ballistic resistant panel to an outer surfaceof a steel pipeline. In other examples, the magnetic attachment featurecan be replaced with any other suitable attachment feature such as, forexample, zippers, snaps, or hook and loop fasteners.

The plurality of ballistic sheets 1005 within flexible ballisticresistant panel 100 for the oil or gas pipeline can include about 1-10,10-20, or 20-30 ballistic sheets. The plurality of ballistic sheets 1005can be made from a plurality of aramid fibers coated with athermoplastic polymer resin. The thermoplastic polymer resin can have amelting temperature of about 215-240, 255-295, or 295-330 degrees F. Thepanel 100 can be manufactured according to any of the manufacturingmethods specifically described herein.

Ballistic Performance Standards

The ballistic resistant panels 100 described herein can be configured tocomply with certain performance standards, such as those set forth inNIJ Standard-0101.06, Ballistic Resistance of Body Armor (July 2008),which is hereby incorporated by reference in its entirety. The NationalInstitute of Justice (NIJ), which is part of the U.S. Department ofJustice (DOJ), is responsible for setting minimum performance standardsfor law enforcement equipment, including minimum performance standardsfor police body armor. Under NIJ Standard-0101.06, personal body armoris classified into five categories (IIA, II, IIIA, III, IV) based onballistic performance of the armor. Type HA armor that is new and unwornis tested with 9 mm Full Metal Jacketed Round Nose (FMJ RN) bullets witha specified mass of 8.0 g (124 gr) and a velocity of 373 m/s±9.1 m/s(1225 ft/s±30 ft/s) and with .40 S&W Full Metal Jacketed (FMJ) bulletswith a specified mass of 11.7 g (180 gr) and a velocity of 352 m/s±9.1m/s (1155 ft/s±30 ft/s). Type II armor that is new and unworn is testedwith 9 mm FMJ RN bullets with a specified mass of 8.0 g (124 gr) and avelocity of 398 m/s±9.1 m/s (1305 ft/s±30 ft/s) and with 0.357 MagnumJacketed Soft Point (JSP) bullets with a specified mass of 10.2 g (158gr) and a velocity of 436 m/s±9.1 m/s (1430 ft/s±30 ft/s). Type IIIAarmor that is new and unworn shall be tested with .357 SIG FMJ Flat Nose(FN) bullets with a specified mass of 8.1 g (125 gr) and a velocity of448 m/s±9.1 m/s (1470 ft/s±30 ft/s) and with .44 Magnum Semi JacketedHollow Point (SJHP) bullets with a specified mass of 15.6 g (240 gr) anda velocity of 436 m/s±9.1 m/s (1430 ft/s±30 ft/s). Type III flexiblearmor shall be tested in both the “as new” state and the conditionedstate with 7.62 mm FMJ, steel jacketed bullets (U.S. Militarydesignation M80) with a specified mass of 9.6 g (147 gr) and a velocityof 847 m/s±9.1 m/s (2780 ft/s±30 ft/s). Type IV flexible armor shall betested in both the “as new” state and the conditioned state with .30caliber AP bullets (U.S. Military designation M2 AP) with a specifiedmass of 10.8 g (166 gr) and a velocity of 878 m/s±9.1 m/s (2880 ft/s±30ft/s).

The term “ballistic limit” describes the impact velocity required toperforate a target with a certain type of projectile. To determine theballistic limit of a target, a series of experimental tests must beconducted. During the tests, the velocity of the certain type ofprojectile is increased until the target is perforated. The term “V₅₀”designates the velocity at which half of the certain type of projectilesfired at the target will penetrate the target and half will not.

Panel Dimensions and Weight

The flexible ballistic resistant panels 100 described herein are lighterand thinner than existing panels with a similar threat levelcertification. For instance, an existing stitched panel certified asType IIIA has a weight of about 1.25 pounds for a 1 foot by 1 foot paneland a thickness of about 0.300 inches. Conversely, the panels 100described herein, which have achieved the same certification, have aweight of about 1.0 pound for a 1 foot by 1 foot panel and a thicknessof about 0.215 inches. A panel that is thinner and lighter is moreversatile and is suitable for a wider range of applications.

The foregoing description has been presented for purposes ofillustration and description. It is not intended to be exhaustive or tolimit the claims to the embodiments disclosed. Other modifications andvariations may be possible in view of the above teachings. Theembodiments were chosen and described to explain the principles of theinvention and its practical application to enable others skilled in theart to best utilize the invention in various embodiments and variousmodifications as are suited to the particular use contemplated. It isintended that the claims be construed to include other alternativeembodiments of the invention except insofar as limited by the prior art.

What is claimed is:
 1. A ballistic resistant panel, comprising: avehicle door including an outer door structure having a gap between aside window and a lip of said outer door structure; a ballisticresistant panel having an outer perimeter sized to fit within a cavityof said vehicle door between said side window and said outer doorstructure; a flexible excess cover portion upwardly extending from a topedge of said ballistic resistant panel, said flexible excess coverportion extending through said gap located between said side window andsaid lip of said outer door structure, said flexible excess coverportion folding over said lip of said outer door structure; and aweatherstrip installed on said lip of said outer door structure, saidweatherstrip securing said flexible excess cover portion against saidlip of said outer door structure.
 2. The ballistic resistant panel ofclaim 1, wherein said ballistic resistant panel has a thickness of lessthan or equal to about 0.24 inches.
 3. The ballistic resistant panel ofclaim 1, wherein said ballistic resistant panel has a real density ofless than or equal to about 1.38 lb/ft².
 4. The ballistic resistantpanel of claim 1, wherein said ballistic resistant panel has a V50rating of 1600 ft/sec or greater for a 0.44 Magnum lead bullet having anominal mass of 15.55 grams and has a V50 rating of 1720 ft/sec orgreater for a 9 mm full metal jacketed bullet having a nominal mass of8.0 grams.
 5. The ballistic resistant panel of claim 1, wherein saidballistic resistant panel has a ballistic performance that meets orexceeds level III-A requirements set forth in NIJ Standard 0101.06. 6.The ballistic resistant panel of claim 1, wherein said ballisticresistant panel disposed in said cavity between said outer doorstructure and said side window of said vehicle door has a bottom edgewhich seats against a bottom edge of said vehicle door.
 7. The ballisticresistant panel of claim 1, further comprising a channel proximate saidbottom edge of said vehicle door, wherein said ballistic resistant paneldisposed in said cavity between said outer door structure and said sidewindow of said vehicle door seats within said channel.
 8. The ballisticresistant panel of claim 1, further comprising a cover disposed oversaid ballistic resistant panel.
 9. The ballistic resistant panel ofclaim 8, wherein said cover forms a waterproof barrier to preventmoisture from reaching said ballistic resistant panel.
 10. The ballisticresistant panel of claim 8, wherein said cover is made from a materialselected from the group consisting of: a non-waterproof material, awaterproof material, a chemically-resistant material, a flame-resistantmaterial, a flame-retardant material, or combinations thereof.
 11. Theballistic resistant panel of claim 8, further comprising at least oneanti-wear strip coupled to a front surface or a back surface of saidcover against which a moving part within said vehicle door may contactwithout breaching said front surface or said back surface of said cover.12. The ballistic resistant panel of claim 1, wherein said ballisticresistant panel has sufficient flexibility to be contoured aroundcomponents within said vehicle door.
 13. The ballistic resistant panelof claim 1, wherein said ballistic resistant panel includes a stack ofballistic resistant sheets comprising: a first plurality of ballisticresistant sheets bonded to each other; and a second plurality ofballistic resistant sheets moveable in relation to each other.
 14. Theballistic resistant panel of claim 13, wherein said first plurality ofballistic resistant sheets includes a first resin with a first meltingtemperature, said second plurality of ballistic resistant sheetsincludes a second resin with a second melting temperature, said secondmelting temperature higher than said first melting temperature.
 15. Theballistic resistant panel of claim 14, wherein upon exposure of saidstack to a temperature between said first and second meltingtemperatures, said first plurality of ballistic resistant sheets bond toeach other.
 16. The ballistic resistant panel of claim 14, furthercomprising: a third plurality of ballistic resistant sheets including athird resin having a third melting temperature; wherein said thirdmelting temperature differs from at least one of said first and secondmelting temperatures.